熔体质量流动速率

200°C/5.0kg

ASTMD1238

g/10min

60

熔体质量流动速率

190°C/2.16kg

ASTMD1238

g/10min

6.0

收缩率

MD

ASTMD955

%

1.1到1.7

脆化温度5

ASTMD746

°C

-68.5

抗张强度3,4

断裂,23°C

ASTMD412

Mpa

6.58

拉伸应力3,4

300%应变,23°C

ASTMD412

Mpa

3.39

拉伸应力3,4

100%应变,23°C

ASTMD412

Mpa

1.93

伸长率3,4

断裂,23°C

ASTMD412

%

650

撕裂强度

ASTMD624

kN/m

38.5

压缩永久变形

23°C,22hr

ASTMD395B

%

24

表观粘度

200°C,11200sec^-1

ASTMD3835

Pa·s

16.7

肖氏硬度

邵氏A,10秒

ASTMD2240

59

UL阻燃等级

1.5mm

UL94

HB