熔体质量流动速率

220°C/10.0kg

ASTMD1238

g/10min

60

收缩率

MD：3.20mm

ASTMD955

%

0.40to0.70

伸长率3

断裂,3.20mm

ASTMD638

%

>20

抗张强度3

屈服,3.20mm

ASTMD638

Mpa

43.1

拉伸模量2

3.20mm

ASTMD638

Mpa

2160

弯曲模量4

6.40mm

ASTMD790

Mpa

2550

弯曲强度4

6.40mm

ASTMD790

Mpa

68.6

伸长率3

屈服,3.20mm

ASTMD638

%

5.0

RTIElec

UL746

°C

80.0

维卡软化温度

ASTMD15255

°C

84.0

热变形温度

1.8MPa,未退火,6.40mm

ASTMD648

°C

77.0

RTIStr

UL746

°C

80.0

热变形温度

0.45MPa,未退火,6.40mm

ASTMD648

°C

84.0

RTIImp

UL746

°C

70.0

23°C,3.20mm

ASTMD256

J/m

260

-30°C,3.20mm

ASTMD256

J/m

78

23°C,6.40mm

ASTMD256

J/m

230

-30°C,6.40mm

ASTMD256

J/m

78

洛氏硬度

R级

ASTMD785

104

UL阻燃等级

2.5mm

UL94

V-0

UL阻燃等级

3.0mm

UL94

V-0