熔体质量流动速率

220°C/10.0kg

ASTMD1238

g/10min

70

收缩率

MD：3.20mm

ASTMD955

%

0.40到0.70

弯曲模量5

6.40mm

ASTMD790

Mpa

2350

拉伸模量3

3.20mm

ASTMD638

Mpa

2160

抗张强度4

屈服,3.20mm

ASTMD638

Mpa

39.2

伸长率4

断裂,3.20mm

ASTMD638

%

>20

弯曲强度5

6.40mm

ASTMD790

Mpa

65.7

伸长率4

屈服,3.20mm

ASTMD638

%

5.0

RTI

UL746

°C

60.0

RTIElec

UL746

°C

60.0

热变形温度

1.8MPa,未退火,6.40mm

ASTMD648

°C

83.0

热变形温度

0.45MPa,未退火,6.40mm

ASTMD648

°C

89.0

RTIImp

UL746

°C

60.0

维卡软化温度

ASTMD15256

°C

90.0

23°C,3.20mm

ASTMD256

J/m

210

-30°C,3.20mm

ASTMD256

J/m

59

23°C,6.40mm

ASTMD256

J/m

160

-30°C,6.40mm

ASTMD256

J/m

49

洛氏硬度

R级

ASTMD785

105

UL阻燃等级

2.0mm

UL94

V-05VB

UL阻燃等级

2.5mm

UL94

V-05VA

UL阻燃等级

1.5mm

UL94

V-0

UL阻燃等级

3.0mm

UL94

V-05VA