模具收缩率

Flow,3.20mm

ASTM D-955

%

0.40-0.70

悬臂梁缺口冲击强度

23℃

179/1eA

KJ/m

13.0

弯曲模量

50.0mm Span

ASTM D-790

Mpa

2600

悬臂梁缺口冲击强度

-30℃

ISO 179/1eA

KJ/m

8.00

拉伸断裂伸长率

ASTM D-638

%

10

拉伸屈服强度

ASTM D-638

Mpa

51.0

IZOD缺口冲击强度

-30℃

ASTM D-256

J/m

60.0

弯曲屈服强度

50.0mm Span

ASTM D-790

Mpa

77.0

拉伸断裂强度

ASTM D-638

Mpa

34.0

肖氏硬度

ASTM D-2240

78

拉伸模量

ASTM D-638

Mpa

2650

拉伸屈服伸长率

ASTM D-638

%

2.8

IZOD缺口冲击强度

23℃

ASTM D-256

J/m

80.0

热变形温度

1.80MPa，未退火，3.20mm

ASTM D-648

°C

83.0

线形热膨胀系数

Transverse,-40TO40℃

ASTM E-831

cm/cm/℃

0.000085

燃烧性

1.50mm

UL 94

HB

维卡软化温度

ASTM D-1525

°C

89.0

线形热膨胀系数

Flow,-40TO40℃

ASTM E-831

cm/cm/℃

0.000087

熔融指数

220℃/10.0kg

ASTM D-1238

g/10min

25