熔体质量流动速率

250°C/5.0kg

ASTMD1238

g/10min

22

收缩率

MD

ASTMD955

%

0.50to0.70

抗张强度2

屈服,3.20mm

ASTMD638

Mpa

61.8

伸长率2

断裂,3.20mm

ASTMD638

%

100

弯曲强度4

屈服,3.20mm

ASTMD790

Mpa

91.2

弯曲模量3

3.20mm

ASTMD790

Mpa

2260

RTIElec

UL746

°C

120

维卡软化温度

ASTMD15254

°C

141

热变形温度

1.8MPa,未退火,6.40mm

ASTMD648

°C

130

RTIStr

UL746

°C

120

RTIImp

UL746

°C

110

相比耐漏电起痕指数

CTI

UL746

PLC3

23°C,3.20mm

ASTMD256

J/m

690

洛氏硬度

R级

ASTMD785

118

UL阻燃等级

2.0mm

UL94

V-1

UL阻燃等级

2.5mm

UL94

V-0

UL阻燃等级

1.5mm

UL94

V-2

UL阻燃等级

3.0mm

UL94

V-0

Transparency

ASTMD1003

%

87