抗张强度

--

ASTMD638

Mpa

31.0

抗张强度

100%应变

ASTMD638

Mpa

2.30

抗张强度

300%应变

ASTMD638

Mpa

3.80

伸长率

断裂,0.762mm

ASTMD638

%

630

玻璃转化温度1

DSC

°C

-31.0

RingandBallSofteningPoint

ASTME28-92

°C

179

KoflerMeltingTemperature

ASTMD1525

°C

85

伸长率

断裂

ASTMD412

%

630

拉伸应力

100%应变

ASTMD412

Mpa

2.30

拉伸应力

300%应变

ASTMD412

Mpa

3.80

抗张强度

断裂

ASTMD412

Mpa

31.0

熔体粘度

204°C

ASTMD1084

Pa·s

92.0

布络克菲尔德粘度2

15%T.S.inMEK/Toluene:23°C

Pa·s

0.250

布络克菲尔德粘度2

15%T.S.inCyclohexanone:23°C

Pa·s

1.60

肖氏硬度

邵氏A

ASTMD2240

70

AdhesiontoPET3

g/2.5cm

305.9

GradientBarTackTemperature

°C

91

OpenTime

ASTMD4497-94

min

>5.0

T-Peel

AluminumFoil

ASTMD1876

kN/m

1.8

T-Peel

MylarFilm

ASTMD1876

kN/m

3.4