TPU-Ether

TPU-Ether Texin® 950 U 德国科思创

0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)

产品描述

典型应用：
管道,管件,鞋类,连接器
颜色：
自然色

物性表

物理性能测试条件测试方法测试结果测试单位
密度-ASTM D7921.15g/cm³
-ISO 11831.15g/cm³
收缩率MD：2.54mmASTM D9550.80%
TD：2.54mmASTM D9550.80%
TD:2.54mmISO 25770.80%
MD:2.54mmISO 25770.80%
机械性能测试条件测试方法测试结果测试单位
弯曲模量70°CASTM D79046.9MPa
23°CISO 178114MPa
70°CISO 17846.9MPa
泰伯耐磨性1000Cycles,1000g,H-18转轮ISO 464975.0mg
1000Cycles,1000g,H-18转轮ASTM D104475.0mg
弯曲模量23°CASTM D790114MPa
热性能测试条件测试方法测试结果测试单位
维卡软化温度-ASTM D15254128°C
-ISO 306/50128°C
线性热膨胀系数MDASTM D6961.3E-04cm/cm/°C
脆化温度-ASTM D746<-68.0°C
-ISO 974<-68.0°C
玻璃转化温度-DMA-27.0°C
弹性体测试条件测试方法测试结果测试单位
伸长率断裂ISO 37470%
撕裂强度-ASTM D624131kN/m
压缩永久变形23°C,22hrASTM D395B20%
70°C,22hr3ASTM D395B40%
70°C,22hrASTM D395B70%
23°C,22hrISO 81520%
23°C,22hr3ISO 81515%
70°C,22hrISO 81570%
70°C,22hr3ISO 81540%
硬度-ASTM D263235%
拉伸强度50%应变ISO 3712.1MPa
50%应变ASTM D41212.1MPa
压缩永久变形23°C,22hr3ASTM D395B15%
拉伸强度100%应变ASTM D41213.8MPa
100%应变ISO 3713.8MPa
300%应变ASTM D41227.6MPa
300%应变ISO 3727.6MPa
屈服ASTM D41249.0MPa
屈服ISO 3749.0MPa
伸长率断裂ASTM D412470%
撕裂强度-ISO 34-1130kN/m
硬度测试条件测试方法测试结果测试单位
硬度邵氏DASTM D224050-
邵氏DISO 86850-
补充信息测试条件测试方法测试结果测试单位
CompressiveLoad10%DeflectionASTM D5755.52MPa
15%DeflectionASTM D5757.58MPa
2%DeflectionASTM D5751.03MPa
20%DeflectionASTM D57510.3MPa
25%DeflectionASTM D57512.4MPa
5%DeflectionASTM D5752.93MPa
50%DeflectionASTM D57531.0MPa
老化测试条件测试方法测试结果测试单位
体积变化23°C,168hr,inReferenceFuelAASTM D4711.0%
23°C,168hr,甲醇ASTM D47126%
23°C,336hr,inReferenceFuelAASTM D4711.0%
23°C,336hr,inReferenceFuelCASTM D47126%
23°C,504hr,inReferenceFuelAASTM D4711.0%
23°C,504hr,inReferenceFuelCASTM D47126%
100°C,70hr,在ASTM#1油中ASTM D4710.0%
空气中硬度(Shore)的变化率ShoreD,100°C,168hr,inASTM#3OilASTM D4715.0-
ShoreD,100°C,336hr,inASTM#1OilASTM D4710.0-
ShoreD,100°C,336hr,inASTM#3OilASTM D471-4.0-
空气中拉伸强度的变化率100°C,336hr,inASTM#3OilASTM D471-3.0%
100%Strain,100°C,336hr,inASTM#3OilASTM D471-2.0%
300%Strain,100°C,336hr,inASTM#3OilASTM D471-9.0%
300%Strain,100°C,504hr,inASTM#1OilISO 175-7.0%
100°C,504hr,inASTM#3OilISO 1751.0%
拉伸应力变化率125°C,336hr，断裂ISO 21612%
125°C,504hr，断裂ISO 2169.0%
空气中硬度(Shore)的变化率ShoreD,100°C,70hrASTM D573-1.0-
ShoreD,100°C,168hrASTM D5730.0-
ShoreD,100°C,336hrASTM D573-2.0-
ShoreD,100°C,504hrASTM D573-1.0-
ShoreD,125°C,70hrASTM D5731.0-
支撐D,125°C,168hrASTM D573-1.0-
ShoreD,125°C,336hrASTM D573-1.0-
ShoreD,125°C,504hrASTM D5731.0-
空气中拉伸强度的变化率300%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ISO 1753.0%
23°C,336hr,inReferenceFuelCISO 175-20%
100%Strain,23°C,336hr,inReferenceFuelCISO 175-36%
300%Strain,23°C,336hr,inReferenceFuelCISO 175-33%
300%Strain,100°C,168hr,inASTM#1OilISO 1750.0%
100°C,168hr,inASTM#3OilISO 17512%
空气中极限伸长率的变化率23°C,504hr,inReferenceFuelA(Isooctane)ASTM D4718.0%
23°C,504hr,inReferenceFuelCASTM D471-2.0%
100°C,70hr,在ASTM#1油中ASTM D47118%
100°C,70hr,在ASTM#3油中ASTM D47117%
100°C,168hr,inASTM#1OilASTM D47119%
100°C,168hr,inASTM#3OilASTM D47125%
100°C,336hr,inASTM#1OilASTM D47123%
100°C,336hr,inASTM#3OilASTM D47127%
100°C,504hr,inASTM#1OilASTM D47132%
100°C,504hr,inASTM#3OilASTM D47138%
空气中拉伸强度的变化率300%Strain,23°C,336hr,inReferenceFuelCASTM D471-33%
23°C,504hr,inReferenceFuelA(Isooctane)ASTM D47113%
100%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ASTM D471-4.0%
300%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ASTM D471-4.0%
23°C,504hr,inReferenceFuelCASTM D471-15%
100°C,504hr,inASTM#1OilASTM D471-3.0%
100%Strain,100°C,504hr,inASTM#1OilASTM D4714.0%
300%Strain,100°C,504hr,inASTM#1OilASTM D471-7.0%
100°C,504hr,inASTM#3OilASTM D4711.0%
100%Strain,100°C,504hr,inASTM#3OilASTM D471-9.0%
300%Strain,100°C,70hrASTM D5732.0%
100°C,168hrASTM D5732.0%
100%Strain,100°C,168hrASTM D5734.0%
300%Strain,100°C,168hrASTM D573-1.0%
100°C,336hrASTM D5734.0%
拉伸应力变化率125°C,168hr，断裂ISO 21629%
空气中拉伸强度的变化率125°C,336hrISO 216-40%
100%Strain125°C,336hrISO 2160.0%
300%Strain125°C,336hrISO 216-22%
125°C,504hrISO 216-44%
100%Strain125°C,504hrISO 216-5.0%
300%Strain125°C,504hrISO 216-25%
空气中极限伸长率的变化率100°C,70hrASTM D57310%
100°C,168hrASTM D57315%
100°C,336hrASTM D57319%
100°C,504hrASTM D57316%
空气中拉伸强度的变化率300%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ASTM D4710.0%
23°C,70hr,甲醇ASTM D471-17%
100°C,70hrASTM D5732.0%
100%Strain,100°C,70hrASTM D5734.0%
125°C,70hrASTM D573-11%
100°C,504hrISO 21638%
100%Strain100°C,504hrISO 2165.0%
300%Strain100°C,504hrISO 216-3.0%
125°C,70hrISO 216-11%
100%Strain125°C,70hrISO 2161.0%
300%Strain125°C,70hrISO 216-7.0%
125°C,168hrISO 216-27%
体积变化23°C,168hr,甲醇ISO 17526%
23°C,336hr,inReferenceFuelAISO 1751.0%
23°C,336hr,inReferenceFuelCISO 17526%
23°C,504hr,inReferenceFuelAISO 1751.0%
100°C,336hr,inASTM#1OilASTM D4710.0%
拉伸应力变化率23°C,70hr,inReferenceFuelA(Isooctane)，断裂ISO 1755.0%
23°C,70hr,甲醇，断裂ISO 1750.0%
23°C,168hr,inReferenceFuelA(Isooctane)，断裂ISO 1757.0%
23°C,168hr,甲醇，断裂ISO 175-6.0%
空气中极限伸长率的变化率23°C,336hr,inReferenceFuelA(Isooctane)ASTM D4713.0%
23°C,336hr,inReferenceFuelCASTM D471-2.0%
空气中硬度(Shore)的变化率ShoreD,23°C,336hr,inReferenceFuelA(Isooctane)ASTM D4710.0-
ShoreD,23°C,336hr,inReferenceFuelCASTM D471-10-
空气中拉伸强度的变化率100%Strain,23°C,504hr,inReferenceFuelCASTM D471-36%
300%Strain,23°C,504hr,inReferenceFuelCASTM D471-51%
100°C,70hr,在ASTM#1油中ASTM D4712.0%
100%Strain,100°C,70hr,inASTM#1OilASTM D4717.0%
300%Strain,100°C,70hr,inASTM#1OilASTM D4710.0%
100°C,70hr,在ASTM#3油中ASTM D47110%
100%Strain,100°C,70hr,inASTM#3OilASTM D4712.0%
300%Strain,100°C,70hr,inASTM#3OilASTM D4713.0%
100°C,168hr,inASTM#1OilASTM D4710.0%
100%Strain,100°C,168hr,inASTM#1OilASTM D4714.0%
100°C,336hr,inASTM#1OilISO 175-2.0%
100%Strain,100°C,336hr,inASTM#1OilISO 1758.0%
300%Strain,100°C,336hr,inASTM#1OilISO 1750.0%
100°C,336hr,inASTM#3OilISO 175-3.0%
100%Strain,100°C,336hr,inASTM#3OilISO 175-2.0%
300%Strain,100°C,336hr,inASTM#3OilISO 175-9.0%
100°C,504hr,inASTM#1OilISO 175-3.0%
100%Strain,100°C,504hr,inASTM#1OilISO 1754.0%
23°C,168hr,甲醇ISO 175-17%
100%Strain,23°C,168hr,inReferenceFuelCISO 175-36%
300%Strain,23°C,168hr,inReferenceFuelCISO 175-30%
23°C,336hr,inReferenceFuelA(Isooctane)ISO 1757.0%
100%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ISO 1751.0%
100%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ISO 175-3.0%
300%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ISO 1750.0%
23°C,70hr,甲醇ISO 175-17%
100°C,70hr,在ASTM#1油中ISO 1752.0%
100%Strain,100°C,70hr,inASTM#1OilISO 1757.0%
300%Strain,100°C,70hr,inASTM#1OilISO 1750.0%
100°C,70hr,在ASTM#3油中ISO 17510%
100%Strain,100°C,70hr,inASTM#3OilISO 1752.0%
300%Strain,100°C,70hr,inASTM#3OilISO 1753.0%
100°C,168hr,inASTM#1OilISO 1750.0%
100%Strain,100°C,168hr,inASTM#1OilISO 1754.0%
100%Strain,100°C,336hrASTM D5734.0%
300%Strain,100°C,336hrASTM D573-2.0%
100°C,504hrASTM D57338%
100%Strain,100°C,504hrASTM D5735.0%
300%Strain,100°C,504hrASTM D573-3.0%
23°C,336hr,inReferenceFuelA(Isooctane)ASTM D4717.0%
100%Strain,23°C,70hr,inReferenceFuelCASTM D471-42%
300%Strain,125°C,336hrASTM D573-22%
125°C,504hrASTM D573-44%
空气中极限伸长率的变化率125°C,70hrASTM D57322%
125°C,168hrASTM D57329%
125°C,336hrASTM D57312%
125°C,504hrASTM D5739.0%
空气中硬度(Shore)的变化率ShoreD,125°C,504hrISO 2161.0-
空气中拉伸强度的变化率23°C,70hr,inReferenceFuelA(Isooctane)ASTM D47116%
100%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ASTM D471-3.0%
300%Strain100°C,168hrISO 216-1.0%
100°C,336hrISO 2164.0%
100%Strain100°C,336hrISO 2164.0%
体积变化100°C,336hr,inASTM#3OilASTM D47112%
100°C,504hr,inASTM#1OilASTM D4710.0%
100°C,504hr,inASTM#3OilASTM D47113%
23°C,504hr,inReferenceFuelCISO 17526%
100°C,70hr,在ASTM#1油中ISO 1750.0%
100°C,70hr,在ASTM#3油中ISO 1759.0%
空气中硬度(Shore)的变化率ShoreD,23°C,70hr,inReferenceFuelA(Isooctane)ASTM D4711.0-
ShoreD,23°C,70hr,inReferenceFuelCASTM D471-11-
ShoreD,23°C,168hr,inReferenceFuelA(Isooctane)ASTM D4711.0-
ShoreD,23°C,168hr,inReferenceFuelCASTM D471-13-
ShoreD,100°C,504hr,inASTM#1OilASTM D4712.0-
ShoreD,100°C,504hr,inASTM#3OilASTM D471-2.0-
体积变化100°C,70hr,在ASTM#3油中ASTM D4719.0%
100°C,168hr,inASTM#1OilASTM D4710.0%
100°C,168hr,inASTM#3OilASTM D47110%
空气中硬度(Shore)的变化率ShoreD,23°C,504hr,inReferenceFuelA(Isooctane)ASTM D4712.0-
ShoreD,23°C,504hr,inReferenceFuelCASTM D471-13-
ShoreD,100°C,70hr,inASTM#1OilASTM D4710.0-
ShoreD,100°C,70hr,inASTM#3OilASTM D4715.0-
ShoreD,100°C,168hr,inASTM#1OilASTM D4712.0-
空气中拉伸强度的变化率300%Strain,100°C,168hr,inASTM#1OilASTM D4710.0%
100°C,168hr,inASTM#3OilASTM D47112%
100%Strain,100°C,168hr,inASTM#3OilASTM D471-7.0%
300%Strain,100°C,168hr,inASTM#3OilASTM D471-11%
100°C,336hr,inASTM#1OilASTM D471-2.0%
100%Strain,100°C,336hr,inASTM#1OilASTM D4718.0%
300%Strain,100°C,336hr,inASTM#1OilASTM D4710.0%
23°C,504hr,inReferenceFuelA(Isooctane)ISO 17513%
100%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ISO 175-4.0%
300%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ISO 175-4.0%
23°C,504hr,inReferenceFuelCISO 175-15%
100%Strain,23°C,504hr,inReferenceFuelCISO 175-36%
300%Strain,23°C,504hr,inReferenceFuelCISO 175-51%
100%Strain,100°C,168hr,inASTM#3OilISO 175-7.0%
300%Strain,100°C,168hr,inASTM#3OilISO 175-11%
300%Strain,100°C,504hr,inASTM#3OilASTM D471-18%
23°C,70hr,inReferenceFuelA(Isooctane)ISO 17516%
100%Strain,125°C,70hrASTM D5731.0%
300%Strain,125°C,70hrASTM D573-7.0%
125°C,168hrASTM D573-27%
100%Strain,125°C,168hrASTM D5734.0%
300%Strain,125°C,168hrASTM D573-18%
125°C,336hrASTM D573-40%
100%Strain,125°C,336hrASTM D5730.0%
300%Strain100°C,336hrISO 216-2.0%
100%应变125°C,168hrISO 2164.0%
300%Strain125°C,168hrISO 216-18%
空气中硬度(Shore)的变化率ShoreD,100°C,70hrISO 216-1.0-
ShoreD,100°C,168hrISO 2160.0-
ShoreD,100°C,336hrISO 216-2.0-
体积变化100°C,168hr,inASTM#1OilISO 1750.0%
100°C,168hr,inASTM#3OilISO 17510%
100°C,336hr,inASTM#1OilISO 1750.0%
100°C,336hr,inASTM#3OilISO 17512%
100°C,504hr,inASTM#1OilISO 1750.0%
100°C,504hr,inASTM#3OilISO 17513%
硬度ShoreD,100°C,70hr,inASTM#1OilISO 1750.0-
ShoreD,100°C,70hr,inASTM#3OilISO 1755.0-
ShoreD,100°C,168hr,inASTM#1OilISO 1752.0-
ShoreD,100°C,168hr,inASTM#3OilISO 1755.0-
ShoreD,100°C,336hr,inASTM#1OilISO 1750.0-
ShoreD,100°C,336hr,inASTM#3OilISO 175-4.0-
ShoreD,100°C,504hr,inASTM#1OilISO 1752.0-
ShoreD,100°C,504hr,inASTM#3OilISO 175-2.0-
体积变化23°C,70hr,inReferenceFuelAASTM D4710.0%
23°C,70hr,甲醇ASTM D47122%
拉伸应力变化率100°C,168hr,inASTM#1Oil，断裂ISO 17519%
100°C,168hr,inASTM#3Oil，断裂ISO 17525%
100°C,336hr,inASTM#1Oil，断裂ISO 17523%
100°C,336hr,inASTM#3Oil，断裂ISO 17527%
100°C,504hr,inASTM#1Oil，断裂ISO 17532%
100°C,504hr,inASTM#3Oil，断裂ISO 17538%
体积变化23°C,70hr,inReferenceFuelAISO 1750.0%
23°C,70hr,甲醇ISO 17522%
23°C,168hr,inReferenceFuelAISO 1751.0%
硬度ShoreD,23°C,70hr,inReferenceFuelA(Isooctane)ISO 1751.0-
ShoreD,23°C,70hr,inReferenceFuelCISO 175-11-
ShoreD,23°C,168hr,inReferenceFuelA(Isooctane)ISO 1751.0-
ShoreD,23°C,168hr,inReferenceFuelCISO 175-13-
ShoreD,23°C,336hr,inReferenceFuelA(Isooctane)ISO 1750.0-
ShoreD,23°C,336hr,inReferenceFuelCISO 175-10-
ShoreD,23°C,504hr,inReferenceFuelA(Isooctane)ISO 1752.0-
ShoreD,23°C,504hr,inReferenceFuelCISO 175-13-
拉伸应力变化率23°C,336hr,inReferenceFuelA(Isooctane)，断裂ISO 1753.0%
23°C,336hr,inReferenceFuelC，断裂ISO 175-2.0%
23°C,504hr,inReferenceFuelA(Isooctane)，断裂ISO 1758.0%
23°C,504hr,inReferenceFuelC，断裂ISO 175-2.0%
100°C,70hr,在ASTM#1油中，断裂ISO 17518%
100°C,70hr,在ASTM#3油中，断裂ISO 17517%
空气中拉伸强度的变化率100%Strain,100°C,504hr,inASTM#3OilISO 175-9.0%
300%Strain,100°C,504hr,inASTM#3OilISO 175-18%
空气中极限伸长率的变化率23°C,70hr,inReferenceFuelA(Isooctane)ASTM D4715.0%
23°C,70hr,甲醇ASTM D4710.0%
23°C,168hr,inReferenceFuelA(Isooctane)ASTM D4717.0%
23°C,168hr,甲醇ASTM D471-6.0%
空气中拉伸强度的变化率100%Strain,23°C,70hr,inReferenceFuelCISO 175-42%
300%Strain,23°C,70hr,inReferenceFuelCISO 175-36%
23°C,168hr,inReferenceFuelA(Isooctane)ISO 17516%
100%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ISO 1756.0%
300%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ISO 1752.0%
100%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ASTM D4711.0%
300%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ASTM D4713.0%
23°C,336hr,inReferenceFuelCASTM D471-20%
100%Strain,23°C,336hr,inReferenceFuelCASTM D471-36%
300%Strain,23°C,70hr,inReferenceFuelCASTM D471-36%
23°C,168hr,inReferenceFuelA(Isooctane)ASTM D47116%
100%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ASTM D4716.0%
300%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ASTM D4712.0%
23°C,168hr,甲醇ASTM D471-17%
100%Strain,23°C,168hr,inReferenceFuelCASTM D471-36%
300%Strain,23°C,168hr,inReferenceFuelCASTM D471-30%
拉伸应力变化率100°C,70hr，断裂ISO 21610%
100°C,168hr，断裂ISO 21615%
100°C,336hr，断裂ISO 21619%
100°C,504hr，断裂ISO 21616%
125°C,70hr，断裂ISO 21622%
空气中硬度(Shore)的变化率ShoreD,100°C,504hrISO 216-1.0-
ShoreD,125°C,70hrISO 2161.0-
支撐D,125°C,168hrISO 216-1.0-
ShoreD,125°C,336hrISO 216-1.0-
空气中拉伸强度的变化率100%Strain,125°C,504hrASTM D573-5.0%
300%Strain,125°C,504hrASTM D573-25%
100°C,70hrISO 2162.0%
100%Strain100°C,70hrISO 2164.0%
300%Strain100°C,70hrISO 2162.0%
100°C,168hrISO 2162.0%
100%Strain100°C,168hrISO 2164.0%

【免责声明】

普拉司网尽最大努力确保此数据的准确性，但是普拉司网对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。

认证信息

暂无认证数据

替代型号推荐

暂无替代型号推荐
该产品暂时没有可推荐的替代型号