ABS J-1200 美国TLC
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 收缩率 | Flow,3.18mm | ASTM D-955 | 0.050 | % |
| 密度 | - | ASTM D-792 | 1.27 | - |
| 收缩率 | Flow,3.18mm | ASTM D-955 | 0.20 | % |
| Flow | ASTM D-955 | 0.080-0.18 | % | |
| 密度 | - | ASTM D-792 | 1.37 | - |
| - | ASTM D-792 | 1.29 | - | |
| - | ASTM D-792 | 1.41 | - | |
| 收缩率 | Flow | ASTM D-955 | 0.060-0.13 | % |
| 密度 | - | ASTM D-792 | 1.10 | - |
| 收缩率 | Flow,3.18mm | ASTM D-955 | 0.30 | % |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸强度 | 23℃，断裂 | ASTM D-638 | 55.2 | MPa |
| 断裂伸长率 | 23℃ | ASTM D-638 | 3.0 | % |
| 弯曲模量 | 23℃ | ASTM D-790 | 3450 | MPa |
| 弯曲强度 | 23℃，断裂 | ASTM D-790 | 82.7 | MPa |
| 弯曲模量 | - | ASTM D-790 | 6480 | MPa |
| 弯曲强度 | 屈服 | ASTM D-790 | 112 | MPa |
| 拉伸模量 | 23℃ | ASTM D-638 | 11000 | MPa |
| 拉伸强度 | - | ASTM D-638 | 100 | MPa |
| 断裂伸长率 | - | ASTM D-638 | 1.0 | % |
| 弯曲模量 | - | ASTM D-790 | 10500 | MPa |
| 弯曲强度 | - | ASTM D-790 | 148 | MPa |
| 拉伸强度 | 23℃，断裂 | ASTM D-638 | 82.7 | MPa |
| 弯曲模量 | 23℃ | ASTM D-790 | 7580 | MPa |
| 弯曲强度 | 23℃，断裂 | ASTM D-790 | 109 | MPa |
| 悬臂梁缺口冲击强度 | 23℃,3.18mm | ASTM D-256 | 32.0 | J/m |
| 弯曲模量 | - | ASTM D-790 | 3450 | MPa |
| 弯曲强度 | - | ASTM D-790 | 82.7 | MPa |
| 悬臂梁缺口冲击强度 | - | ASTM D-256 | 58.7 | J/m |
| 洛氏硬度 | - | ASTM D-785 | 59 | M scale |
| 拉伸模量 | - | ASTM D-638 | 5170 | MPa |
| 拉伸强度 | 屈服 | ASTM D-638 | 83.4 | MPa |
| 屈服伸长率 | - | ASTM D-638 | 2.7 | % |
| 悬臂梁缺口冲击强度 | - | ASTM D-256 | 32.0 | J/m |
| 洛氏硬度 | - | ASTM D-785 | 64 | M scale |
| 拉伸模量 | - | ASTM D-638 | 6000 | MPa |
| 拉伸强度 | 屈服 | ASTM D-638 | 91.7 | MPa |
| 屈服伸长率 | - | ASTM D-638 | 2.7 | % |
| 弯曲模量 | - | ASTM D-790 | 7240 | MPa |
| 弯曲强度 | 屈服 | ASTM D-790 | 114 | MPa |
| 洛氏硬度 | - | ASTM D-785 | 60 | M scale |
| 拉伸强度 | - | ASTM D-638 | 55.2 | MPa |
| 断裂伸长率 | - | ASTM D-638 | 3.0 | % |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 热变形温度 | 0.45MPa，未退火 | ASTM D-648 | 101 | ℃ |
| 1.80MPa，未退火 | ASTM D-648 | 100 | ℃ | |
| 燃烧性 | 1.59mm | UL 94 | V-0 | - |
| 线性热膨胀系数 | Flow | ASTM D-648 | 0.000018 | ℃ |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 101 | ℃ |
| 燃烧性 | 1.59mm | UL 94 | V-0 | - |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 102 | ℃ |
| 1.80MPa，未退火 | ASTM D-648 | 98.9 | ℃ | |
| 燃烧性 | 1.59mm | UL 94 | V-0 | - |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 96.1 | ℃ |
| 0.45MPa，未退火 | ASTM D-648 | 107 | ℃ | |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 表面电阻率 | - | ASTM D-257 | 5E+02 | ohms |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 吸水率 | 24hr | ASTM D-570 | 0.22 | % |
| 24hr | ASTM D-570 | 0.21 | % | |
| 24hr | ASTM D-570 | 0.30 | % |