产品描述
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 密度 | - | ASTM D792 | 0.930 | g/cm³ |
| Crystallinity | 762.0µm | ASTM D3417 | 48 | % |
| 1.52mm | ASTM D3417 | 47 | % | |
| 3.18mm | ASTM D3417 | 50 | % | |
| 相对粘度 | 762.0µm | ASTM D4020 | 230to350 | cm³/g |
| 1.52mm | ASTM D4020 | 230to350 | cm³/g | |
| 3.18mm | ASTM D4020 | 230to350 | cm³/g | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸强度 | 屈服,0.762mm | ASTM D638 | 23.0 | MPa |
| 屈服,1.52mm | ASTM D638 | 20.0 | MPa | |
| 屈服,3.18mm | ASTM D638 | 22.0 | MPa | |
| 断裂,0.762mm | ASTM D638 | 53.0 | MPa | |
| 断裂,1.52mm | ASTM D638 | 49.0 | MPa | |
| 摩擦系数 | 与自身-静态2 | ASTM D1894 | 0.16 | - |
| 与自身-静态6 | ASTM D1894 | 0.16 | - | |
| 与自身-静态7 | ASTM D1894 | 0.16 | - | |
| 拉伸模量 | 0.762mm | ASTM D638 | 725 | MPa |
| 1.52mm | ASTM D638 | 731 | MPa | |
| 3.18mm | ASTM D638 | 672 | MPa | |
| 拉伸强度 | 断裂,3.18mm | ASTM D638 | 44.0 | MPa |
| 伸长率 | 断裂,0.762mm | ASTM D638 | 60 | % |
| 断裂,1.52mm | ASTM D638 | 460 | % | |
| 断裂,3.18mm | ASTM D638 | 470 | % | |
| 摩擦系数 | 与钢-动态3 | ASTM D1894 | 0.10to0.22 | - |
| 与钢-动态4 | ASTM D1894 | 0.050to0.10 | - | |
| 与钢-动态5 | ASTM D1894 | 0.050to0.080 | - | |
| 与自身-动态2 | ASTM D1894 | 0.14 | - | |
| 与自身-动态6 | ASTM D1894 | 0.13 | - | |
| 与自身-动态7 | ASTM D1894 | 0.14 | - | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 熔融温度 | --6 | - | 134 | °C |
| --2 | - | 136 | °C | |
| 线性热膨胀系数 | MD：-100到-20°C,3.18mm | ASTM D696 | 9.2E-04 | cm/cm/°C |
| MD：20到100°C,3.18mm | ASTM D696 | 1.5E-04 | cm/cm/°C | |
| 电气性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 表面电阻率 | 0.762mm | ASTM D257 | 1E+03 | ohms |
| 1.52mm | ASTM D257 | 1E+03 | ohms | |
| 3.18mm | ASTM D257 | 1E+03 | ohms | |
| 体积电阻率 | 0.762mm | ASTM D257 | 6E+07 | ohms·cm |
| 耗散因数 | 1.52mm,10kHz | ASTM D150 | -2E-03 | - |
| 3.18mm,10kHz | ASTM D150 | 0.0 | - | |
| 3.18mm,5MHz | ASTM D150 | 1E-03 | - | |
| StaticDecay | 762.0µm | - | <10 | msec |
| 1.52mm | - | <10 | msec | |
| 耗散因数 | 1.52mm,5MHz | ASTM D150 | -1E-03 | - |
| StaticDecay | 3.18mm | - | <10 | msec |
| 体积电阻率 | 1.52mm | ASTM D257 | 1.5E+07 | ohms·cm |
| 3.18mm | ASTM D257 | >2.0E+7 | ohms·cm | |
| 介电强度 | 3.18mm | ASTM D149 | 14 | kV/mm |
| 介电常数 | 0.762mm | ASTM D150 | 2.39 | - |
| 1.52mm | ASTM D150 | 2.29 | - | |
| 3.18mm | ASTM D150 | 2.28 | - | |
| 耗散因数 | 0.762mm,10kHz | ASTM D150 | -1E-03 | - |
| 0.762mm,5MHz | ASTM D150 | -1E-03 | - | |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 硬度 | 邵氏D,0.762mm | ASTM D2240 | 65 | - |
| 邵氏D,1.52mm | ASTM D2240 | 65 | - | |
| 邵氏D,3.18mm | ASTM D2240 | 65 | - | |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 悬臂梁缺口冲击强度 | 3.18mm | ASTM D256 | 80 | J/m |
【免责声明】
普拉司网尽最大努力确保此数据的准确性，但是普拉司网对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。