Ethylene Copolymer Ultrathene® UE672 美国利安德巴塞尔
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
特性：
热性能
物性表
| 测试条件 | 测试方法 | 测试结果 | 测试单位 | |
|---|---|---|---|---|
| 熔融温度 | - | DSC | 96.4 | °C |
| 熔体质量流动速率 | 190°C/2.16kg | ASTM D1238 | 0.45 | g/10min |
| 醋酸乙烯含量 | - | - | 12.5 | wt% |
| 薄膜厚度 | - | - | 38 | µm |
| 割线模量 | 1%正割,MD:38µm | ASTM D882 | 80.7 | MPa |
| 1%正割,TD:38µm | ASTM D882 | 88.9 | MPa | |
| 拉伸强度 | MD:屈服,38µm | ASTM D882 | 11.3 | MPa |
| TD:屈服,38µm | ASTM D882 | 5.58 | MPa | |
| MD:断裂,38µm | ASTM D882 | 38.7 | MPa | |
| 雾度 | 38.1µm | ASTM D1003 | 1.2 | % |
| 光泽度 | 45°,38.1µm | ASTM D2457 | 85 | - |
| 透明度 | 38.1µm | ASTM D1746 | 82.0 | - |
| 拉伸强度 | TD:断裂,38µm | ASTM D882 | 32.2 | MPa |
| 伸长率 | MD:屈服,38µm | ASTM D882 | 59 | % |
| TD:屈服,38µm | ASTM D882 | 10 | % | |
| MD:断裂,38µm | ASTM D882 | 470 | % | |
| TD:断裂,38µm | ASTM D882 | 650 | % | |
| 埃尔曼多夫撕裂强度 | MD:38µm | ASTM D1922 | 56 | g |
| TD:38µm | ASTM D1922 | 150 | g | |
| 脆化温度 | - | ASTM D746 | -76.0 | °C |
| 维卡软化温度 | - | ASTM D1525 | 80.0 | °C |