PA6 Ultramid® 8200HS BK102 德国巴斯夫
91
参考价： 24,150 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
典型应用：
汽车应用,齿轮
特性：
热稳定,高强度,耐油
等级：
注塑级
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 吸水率 | 23°C,24hr | ISO 62 | 1.6 | % |
| 24hr | ASTM D570 | 1.6 | % | |
| 收缩率 | MD：3.18mm | - | 1.2 | % |
| 吸水率 | 平衡,50%RH | ASTM D570 | 2.7 | % |
| 平衡,23°C,50%RH | ISO 62 | 2.7 | % | |
| 饱和,23°C | ISO 62 | 9.5 | % | |
| 饱和 | ASTM D570 | 9.5 | % | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 伸长率 | 屈服,23°C | ASTM D638 | 20 | % |
| 屈服,-40°C | ASTM D638 | 3.0 | % | |
| 拉伸强度 | 屈服,120°C | ISO 527-2 | 23.0 | Mpa |
| 屈服,23°C | ISO 527-2 | 80.0 | Mpa | |
| 屈服,-40°C | ISO 527-2 | 136 | Mpa | |
| Yield,121°C | ASTM D638 | 23.0 | Mpa | |
| 屈服,23°C | ASTM D638 | 85.0 | Mpa | |
| 屈服,-40°C | ASTM D638 | 136 | Mpa | |
| 拉伸模量 | 23°C | ISO 527-2 | 2700 | Mpa |
| 弯曲模量 | 65°C | ASTM D790 | 460 | Mpa |
| 90°C | ASTM D790 | 350 | Mpa | |
| 伸长率 | 断裂,-40°C | ASTM D638 | 8.0 | % |
| 断裂,23°C | ASTM D638 | 60 | % | |
| Break,121°C | ASTM D638 | >100 | % | |
| 弯曲模量 | 121°C | ASTM D790 | 305 | Mpa |
| 23°C | ISO 178 | 2400 | Mpa | |
| 弯曲强度 | -40°C | ASTM D790 | 168 | Mpa |
| 23°C | ISO 178 | 82.0 | Mpa | |
| 伸长率 | Yield,121°C | ASTM D638 | 15 | % |
| 拉伸应变 | 屈服,23°C | ISO 527-2 | 5.0 | % |
| 弯曲强度 | 23°C | ASTM D790 | 110 | Mpa |
| 65°C | ASTM D790 | 30.0 | Mpa | |
| 90°C | ASTM D790 | 20.0 | Mpa | |
| 121°C | ASTM D790 | 18.0 | Mpa | |
| 标称拉伸断裂应变 | -40°C | ISO 527-2 | 8.0 | % |
| 23°C | ISO 527-2 | 25 | % | |
| 120°C | ISO 527-2 | >100 | % | |
| 弯曲模量 | -40°C | ASTM D790 | 3010 | Mpa |
| 23°C | ASTM D790 | 2830 | Mpa | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| RTI Imp | 3.0mm | UL 746 | 105 | °C |
| 6.0mm | UL 746 | 105 | °C | |
| 1.3mm | UL 746 | 105 | °C | |
| 0.71mm | UL 746 | 95.0 | °C | |
| RTI Elec | 6.0mm | UL 746 | 130 | °C |
| 3.0mm | UL 746 | 130 | °C | |
| 1.3mm | UL 746 | 130 | °C | |
| 0.71mm | UL 746 | 130 | °C | |
| 线性热膨胀系数 | MD | ASTME831 | 8.3E-05 | cm/cm/°C |
| 熔融温度 | - | ISO 3146 | 220 | °C |
| RTI Str | 0.71mm | UL 746 | 95.0 | °C |
| 1.3mm | UL 746 | 105 | °C | |
| 3.0mm | UL 746 | 105 | °C | |
| 6.0mm | UL 746 | 105 | °C | |
| 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 175 | °C |
| 0.45MPa,未退火 | ISO 75-2/B | 150 | °C | |
| 1.8MPa,未退火 | ASTM D648 | 65.0 | °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 60.0 | °C | |
| 熔融温度 | - | ASTM D3418 | 220 | °C |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 洛氏硬度 | R级 | ASTM D785 | 119 | - |
| 可燃性 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| UL阻燃等级 | 3.0mm | UL 94 | V-2 | - |
| 6.0mm | UL 94 | V-2 | - | |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 简支梁无缺口冲击强度 | 23°C | ISO 179 | NoBreak | - |