完善物性
Copolyester Embrace™ Copolyester 美国Eastman
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 密度 | - | ASTM D1505 | 1.30 | g/cm³ |
| 表面张力 | HarmonicMean,Dispersive:23°C,50.0µm | - | 38 | mN/m |
| HarmonicMean,Polar:23°C,50.0µm | - | 9.0 | mN/m | |
| HarmonicMean,Total:23°C,50.0µm | - | 47 | mN/m | |
| 固有粘度 | 23°C,50.0µm | Internal Method | 0.70 | - |
| 23°C,250.0µm | Internal Method | 0.70 | - | |
| Color | a:50.0µm | ASTM D2244 | 0.020 | - |
| b:50.0µm | ASTM D2244 | 0.37 | - | |
| L:50.0µm | ASTM D2244 | 96 | - | |
| 密度 | - | ASTM D792 | 1.27 | g/cm³ |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 弯曲模量 | 23°C | ASTM D790 | 2100 | MPa |
| 弯曲强度 | 23°C | ASTM D790 | 68.0 | MPa |
| 拉伸强度 | 屈服,23°C | ASTM D638 | 50.0 | MPa |
| 断裂,23°C | ASTM D638 | 28.0 | MPa | |
| 伸长率 | 屈服,23°C | ASTM D638 | 4.0 | % |
| 断裂,23°C | ASTM D638 | 110 | % | |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 雾度 | 50.0µm | ASTM D1003 | 4.9 | % |
| 250µm | ASTM D1003 | 4.9 | % | |
| - | ASTM D1003 | 0.60 | % | |
| 光泽度 | 60°,50.0µm | ASTM D2457 | 139 | - |
| 60°,250µm | ASTM D2457 | 166 | - | |
| 透射率 | 常规,50.0µm | ASTM D1003 | 85.0 | % |
| 总计,50.0µm | ASTM D1003 | 92.0 | % | |
| 常规,250µm | ASTM D1003 | 89.0 | % | |
| 总计,250µm | ASTM D1003 | 92.0 | % | |
| 透明度 | 50.0µm | ASTM D1746 | 85.0 | - |
| 250µm | ASTM D1746 | 67.0 | - | |
| 光泽度 | 60° | ASTM D2457 | 152 | - |
| 透射率 | 总计 | ASTM D1003 | 90.0 | % |
| Regular | ASTM D1003 | 87.0 | % | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 玻璃转化温度 | - | ASTM D1525 | 71.0 | °C |
| 维卡软化温度 | - | ASTM D1525 | 71.0to74.0 | °C |
| 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 70.0 | °C |
| 1.8MPa,未退火 | ASTM D648 | 62.0 | °C | |
| 维卡软化温度 | - | ASTM D15252 | 83.0 | °C |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 洛氏硬度 | R计秤,23°C | ASTM D785 | 108 | - |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 悬臂梁缺口冲击强度 | -40°C | ASTM D256 | 53 | J/m |
| 23°C | ASTM D256 | 94 | J/m | |
| -40°C | ASTM D4812 | NoBreak | - | |
| 23°C | ASTM D4812 | NoBreak | - | |
| 落镖冲击 | -40°C,EnergyatPeakLoad | ASTM D3763 | 35.0 | J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 36.0 | J | |
| 补充信息 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 收缩率 | 90°C,50.0µm | - | 80 | % |
| 撕裂强度 | MD:23°C,250.0µm | ASTM D2582 | 61 | N |
| TD:23°C,250.0µm | ASTM D2582 | 66 | N | |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 割线模量 | MD:50µm | ASTM D882 | 1800 | MPa |
| MD:250µm | ASTM D882 | 1570 | MPa | |
| TD:50µm | ASTM D882 | 7250 | MPa | |
| TD:250µm | ASTM D882 | 1560 | MPa | |
| 拉伸强度 | MD:断裂,50µm | ASTM D882 | 42.0 | MPa |
| 埃尔曼多夫撕裂强度 | MD:50µm | ASTM D1922 | 120 | g |
| MD:250µm | ASTM D1922 | 760 | g | |
| TD:50µm | ASTM D1922 | 12 | g | |
| TD:250µm | ASTM D1922 | 760 | g | |
| 氧气透过率 | 30°C,50µm,68%RH | ASTM D3985 | 71 | cm³·mm/m²/atm/24hr |
| 30°C,250µm,68%RH | ASTM D3985 | 5.9 | cm³·mm/m²/atm/24hr | |
| 薄膜厚度 | - | - | 50250 | µm |
| 伸长率 | TD:断裂,250µm | ASTM D882 | 5.0 | % |
| 落镖冲击 | 23°C,50µm | ASTM D1709A | 230 | g |
| 23°C,250µm | ASTM D1709A | 360 | g | |
| 拉伸强度 | TD:断裂,250µm | ASTM D882 | 53.0 | MPa |
| 伸长率 | MD:断裂,50µm | ASTM D882 | 270 | % |
| MD:断裂,250µm | ASTM D882 | 5.0 | % | |
| 水蒸气透过率 | 38°C,100%RH,50µm | ASTMF1249 | 20 | g/m²/24hr |
| 38°C,100%RH,250µm | ASTMF1249 | 7.6 | g/m²/24hr | |
| 撕裂强度 | MD:23°C,250.0µm | ASTM D1938 | 61 | kN/m |
| TD:23°C,250.0µm | ASTM D1938 | 61 | kN/m | |
| 伸长率 | TD:断裂,50µm | ASTM D882 | 34 | % |
| 拉伸强度 | MD:断裂,250µm | ASTM D882 | 53.0 | MPa |
| TD:断裂,50µm | ASTM D882 | 290 | MPa |
【免责声明】
普拉司网尽最大努力确保此数据的准确性，但是普拉司网对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。
认证信息
暂无认证数据
替代型号推荐
暂无替代型号推荐
该产品暂时没有可推荐的替代型号