完善物性
Ethylene Copolymer 500LC 比利时索尔维
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
特性：
热性能
物性表
| 测试条件 | 测试方法 | 测试结果 | 测试单位 | |
|---|---|---|---|---|
| 脆化温度 | - | ASTM D746A | <-76.0 | °C |
| 线性热膨胀系数 | MD | ASTM D696 | 1E-04 | cm/cm/°C |
| 比热 | 23°C | ASTM D3418 | 962 | J/kg/°C |
| 导热系数 | 40°C | ASTMC177 | 0.15 | W/m/K |
| 体积电阻率 | 23°C | ASTM D257 | 5.5E+16 | ohms·cm |
| 介电强度 | 23°C,3.20mm | ASTM D149 | 14 | kV/mm |
| 介电常数 | 23°C,1MHz | ASTM D150 | 2.57 | - |
| 极限氧指数 | - | ASTM D2863 | 52 | % |
| 割线模量 | MD | ASTM D882 | 1550 | MPa |
| TD | ASTM D882 | 1500 | MPa | |
| 拉伸强度 | MD:屈服 | ASTM D882 | 34.5 | MPa |
| 摩擦系数 | 与自身-静态 | ASTM D1894 | 0.20 | - |
| 泰伯耐磨性(1000Cycles,500g,CS-17转轮) | ASTM D1894 | 5.00 | mg | |
| 撕裂强度 | MD (纵向) | ASTM D1004 | 5.72 | - |
| 薄膜厚度 | -- | - | 50 | µm |
| --2 | - | 50 | µm | |
| --3 | - | 130 | µm | |
| 悬臂梁缺口冲击强度 | 23°C | ASTM D256 | NB | J/m |
| -40°C | ASTM D256 | 2.10 | J/m | |
| 摩擦系数 | 动态 | ASTM D3702 | 0.20 | - |
| 静态 | ASTM D3702 | 0.30 | - | |
| 泰伯磨损 | ASTM D1044 | 5.0 | mg/1000Cycles | |
| 密度 | - | ASTM D792 | 1.68 | g/cm³ |
| 收缩率 | MD | ASTM D995 | 2.5 | % |
| 熔体质量流动速率 | 275℃/2.16Kg | ASTM D1238 | 18 | g/10min |
| 饱和吸水量 | ASTM D570 | <=0.10 | % | |
| 洛氏硬度 | - | ASTM D785 | 90 | R |
| 硬度 | - | ASTM D2240 | 75 | - |
| 拉伸强度 | 断裂，50mm/min，23°C | ASTM D638 | 47.0 | MPa |
| 线性热膨胀系数 | 比热容 | ASTMC351 | 962 | J/Kg/°C |
| 融合热 | ASTM D3418 | 42.0 | J/g | |
| 体积电阻率 | - | ASTM D257 | 1E+16 | Ω.cm |
| 介电强度 | 3.18mm | ASTM D149 | 22 | KV/mm |
| 拉伸强度 | 屈服，50mm/min，23°C | ASTM D638 | 30.0 | MPa |
| 断裂伸长率 | 50mm/min，23°C | ASTM D638 | 250 | % |
| 拉伸模量 | 50mm/min，23°C | ASTM D638 | 1660 | MPa |
| 维卡软化温度 | 玻璃转化温度 | ASTM D648 | 85.0 | °C |
| 熔融温度 | - | 242 | °C | |
| 线性热膨胀系数 | MD | ASTM D696 | 1E-02 | cm/cm／°C |
| 脆化温度 | ASTM D746 | <=-76.0 | °C | |
| 导热系数 | JISR2618 | 0.150 | W/m/K | |
| 结晶温度 | ASTM D3418 | 222 | °C | |
| 弯曲强度 | 2.5mm/min，23°C | ASTM D790 | 47.0 | MPa |
| 弯曲模量 | 2.5mm/min，23°C | ASTM D790 | 1690 | MPa |
| 玻璃转化温度 | - | DMA | 85.0 | °C |
| 熔融温度 | - | ASTM D3418 | 242 | °C |
| 拉伸强度 | TD:断裂 | ASTM D882 | 50.0 | MPa |
| 伸长率 | MD:屈服 | ASTM D882 | 6.0 | % |
| MD:断裂 | ASTM D882 | 280 | % | |
| TD:断裂 | ASTM D882 | 280 | % | |
| 落镖冲击 | - | ASTM D1709B | 610 | g |
| 水蒸气透过率 | - | ASTMF1249 | 1.6 | g·mm/m²/atm/24hr |
| 自由收缩 | 200°C | ASTM D2732 | 4.4 | % |
| 撕裂强度 | MD (纵向) | ASTM D1922 | >6400 | gf |
| 面积系数 | - | - | 115 | ft²/lb/mil |
| 拉伸强度 | MD:断裂 | ASTM D882 | 53.0 | MPa |
| 密度 | - | ASTM D792 | 1.68 | g/cm³ |
| 吸水率 | 平衡 | ASTM D570 | <0.10 | % |
| 摩擦系数 | 与自身-动态 | ASTM D1894 | 0.20 | - |
| 结晶峰温度 | DSC | ASTM D3418 | 222 | °C |
| 摩擦系数 | 屈服伸长率 | ASTM D638 | 5.0 | % |
| 热变形温度 | 0.45MPa未退火 | ASTM D648 | 90.0 | °C |
| 1.80MPa未退火 | ASTM D648 | 65.0 | °C | |
| 介电常数 | - | ASTM D150 | 2.57 | 1MHz |
| UL阻燃等级 | - | UL -94 | V-0 | 0.18mm |
| - | UL -94 | V-0 | 1.50mm | |
| - | UL -94 | V-0 | 3.00mm | |
| 极限氧指数 | - | ASTM2863 | 52 | % |