TPU Desmopan® 255 德国科思创（拜耳）
157
参考价： 90,390 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
典型应用：
齿轮,汽车领域,机械部件,体育用品,凸轮,液压应用,车轮,垫圈,齿轮,密封件
特性：
耐磨,抗化学,高强度
等级：
注塑级
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 收缩率 | TD：2.54mm | ASTM D955 | 0.80 | % |
| MD：2.54mm | ASTM D955 | 0.80 | % | |
| MD:2.54mm | ISO 2577 | 0.80 | % | |
| TD:2.54mm | ISO 2577 | 0.80 | % | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 泰伯耐磨性 | 1000Cycles,1000g,H-18转轮 | ISO 4649 | 50.0 | mg |
| 剪切强度 | - | ASTM D732 | 38.5 | Mpa |
| 弯曲模量 | 70°C | ISO 178 | 51.7 | Mpa |
| 23°C | ISO 178 | 68.9 | Mpa | |
| -30°C | ISO 178 | 1210 | Mpa | |
| 70°C | ASTM D790 | 51.7 | Mpa | |
| 23°C | ASTM D790 | 68.9 | Mpa | |
| -30°C | ASTM D790 | 1210 | Mpa | |
| 泰伯耐磨性 | 1000Cycles,1000g,H-18转轮 | ASTM D1044 | 50.0 | mg |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 脆化温度 | - | ISO 974 | <-68.0 | °C |
| 玻璃转化温度 | - | DMA | -26.0 | °C |
| 维卡软化温度 | - | ASTM D15255 | 168 | °C |
| 线性热膨胀系数 | MD | ASTM D696 | 1.3E-04 | cm/cm/°C |
| 维卡软化温度 | - | ISO 306/50 | 168 | °C |
| 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 59.0 | °C |
| 0.45MPa,未退火 | ISO 75-2/B | 59.0 | °C | |
| 脆化温度 | - | ASTM D746 | <-68.0 | °C |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸强度 | 300%应变 | ASTM D412 | 32.4 | Mpa |
| 100%应变 | ISO 37 | 15.9 | Mpa | |
| 100%应变 | ASTM D412 | 15.9 | Mpa | |
| 撕裂强度 | - | ISO 34-1 | 160 | kN/m |
| - | ASTM D624 | 158 | kN/m | |
| 伸长率 | 断裂 | ISO 37 | 500 | % |
| 断裂 | ASTM D412 | 500 | % | |
| 拉伸强度 | 屈服 | ISO 37 | 63.4 | Mpa |
| 屈服 | ASTM D412 | 63.4 | Mpa | |
| 300%应变 | ISO 37 | 32.4 | Mpa | |
| 压缩永久变形 | 70°C,22hr | ASTM D395B | 65 | % |
| 100°C,22hr3 | ASTM D395B | 50 | % | |
| 100°C,22hr | ASTM D395B | 75 | % | |
| 23°C,22hr3 | ISO 815 | 15 | % | |
| 23°C,22hr | ISO 815 | 20 | % | |
| 70°C,22hr3 | ISO 815 | 35 | % | |
| 70°C,22hr | ISO 815 | 65 | % | |
| 23°C,22hr3 | ASTM D395B | 15 | % | |
| 拉伸强度 | 50%应变 | ASTM D412 | 12.4 | Mpa |
| 50%应变 | ISO 37 | 12.4 | Mpa | |
| 压缩永久变形 | 23°C,22hr | ASTM D395B | 20 | % |
| 70°C,22hr3 | ASTM D395B | 35 | % | |
| 100°C,22hr | ISO 815 | 75 | % | |
| 100°C,22hr3 | ISO 815 | 50 | % | |
| 硬度 | - | ASTM D2632 | 40 | % |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 硬度 | 邵氏D | ASTM D2240 | 55 | - |
| 邵氏D | ISO 868 | 55 | - | |
| 可燃性 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| UL阻燃等级 | 1.5mm | UL 94 | HB | - |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 落镖冲击 | -30°C,2.54mm,TotalEnergy | ASTM D3763 | 50.0 | J |
| 23°C,2.54mm,TotalEnergy | ASTM D3763 | 57.8 | J | |
| 补充信息 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| CompressiveLoad | 2%Deflection | ASTM D575 | 0.965 | Mpa |
| 20%Deflection | ASTM D575 | 12.7 | Mpa | |
| 10%Deflection | ASTM D575 | 7.41 | Mpa | |
| 15%Deflection | ASTM D575 | 10.1 | Mpa | |
| 50%Deflection | ASTM D575 | 40.6 | Mpa | |
| 25%Deflection | ASTM D575 | 15.5 | Mpa | |
| 5%Deflection | ASTM D575 | 3.90 | Mpa | |
| 老化 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 空气中拉伸强度的变化率 | 300%Strain,100°C,168hr | ASTM D573 | -5.0 | % |
| 100°C,336hr | ASTM D573 | 14 | % | |
| 100%Strain,100°C,336hr | ASTM D573 | 13 | % | |
| 300%Strain,100°C,336hr | ASTM D573 | -1.0 | % | |
| 100°C,504hr | ASTM D573 | 14 | % | |
| 100%Strain,100°C,504hr | ASTM D573 | 14 | % | |
| 300%Strain,100°C,504hr | ASTM D573 | 1.0 | % | |
| 125°C,70hr | ASTM D573 | -20 | % | |
| 100%Strain,125°C,70hr | ASTM D573 | 7.0 | % | |
| 300%Strain,125°C,70hr | ASTM D573 | -23 | % | |
| 300%Strain100°C,70hr | ISO 216 | 1.0 | % | |
| 100°C,168hr | ASTM D573 | 8.0 | % | |
| 100%Strain,100°C,168hr | ASTM D573 | 4.0 | % | |
| 100°C,168hr | ISO 216 | 8.0 | % | |
| 125°C,504hr | ISO 216 | -27 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,125°C,168hr | ISO 216 | 0.0 | - |
| ShoreD,125°C,336hr | ISO 216 | -5.0 | - | |
| ShoreD,125°C,504hr | ISO 216 | -4.0 | - | |
| 空气中拉伸强度的变化率 | 23°C,70hr,inReferenceFuelA(Isooctane) | ASTM D471 | 6.0 | % |
| 100%Strain,23°C,70hr,inReferenceFuelA(Isooctane) | ASTM D471 | 2.0 | % | |
| 100%Strain100°C,70hr | ISO 216 | 11 | % | |
| 100%Strain100°C,168hr | ISO 216 | 4.0 | % | |
| 100°C,70hr | ASTM D573 | 3.0 | % | |
| 100%Strain,100°C,70hr | ASTM D573 | 11 | % | |
| 300%Strain,100°C,70hr | ASTM D573 | 1.0 | % | |
| 300%Strain100°C,168hr | ISO 216 | -5.0 | % | |
| 100°C,336hr | ISO 216 | 14 | % | |
| 100%Strain100°C,336hr | ISO 216 | 13 | % | |
| 300%Strain100°C,336hr | ISO 216 | -1.0 | % | |
| 100°C,504hr | ISO 216 | 14 | % | |
| 100%Strain100°C,504hr | ISO 216 | 14 | % | |
| 空气中硬度(Shore)的变化率 | ShoreD,100°C,504hr | ISO 216 | 0.0 | - |
| ShoreD,125°C,70hr | ISO 216 | 1.0 | - | |
| 拉伸应力变化率 | 100°C,168hr，断裂 | ISO 216 | 7.0 | % |
| 100°C,336hr，断裂 | ISO 216 | 14 | % | |
| 空气中拉伸强度的变化率 | 100%Strain125°C,504hr | ISO 216 | 4.0 | % |
| 300%Strain125°C,504hr | ISO 216 | -30 | % | |
| 空气中极限伸长率的变化率 | 100°C,70hr | ASTM D573 | -3.0 | % |
| 100°C,168hr | ASTM D573 | 7.0 | % | |
| 100°C,336hr | ASTM D573 | 14 | % | |
| 100°C,504hr | ASTM D573 | 15 | % | |
| 125°C,70hr | ASTM D573 | 28 | % | |
| 125°C,168hr | ASTM D573 | 24 | % | |
| 拉伸应力变化率 | 100°C,70hr，断裂 | ISO 216 | -3.0 | % |
| 100°C,504hr，断裂 | ISO 216 | 15 | % | |
| 125°C,70hr，断裂 | ISO 216 | 28 | % | |
| 125°C,168hr，断裂 | ISO 216 | 24 | % | |
| 125°C,336hr，断裂 | ISO 216 | 35 | % | |
| 125°C,504hr，断裂 | ISO 216 | 30 | % | |
| 空气中硬度(Shore)的变化率 | ShoreD,100°C,70hr | ASTM D573 | -2.0 | - |
| 空气中极限伸长率的变化率 | 125°C,336hr | ASTM D573 | 35 | % |
| 125°C,504hr | ASTM D573 | 30 | % | |
| 空气中拉伸强度的变化率 | 125°C,504hr | ASTM D573 | -27 | % |
| 100%Strain,125°C,504hr | ASTM D573 | 4.0 | % | |
| 100%Strain,125°C,336hr | ASTM D573 | 8.0 | % | |
| 300%Strain,125°C,336hr | ASTM D573 | -27 | % | |
| 125°C,168hr | ASTM D573 | -11 | % | |
| 100%Strain,125°C,168hr | ASTM D573 | -2.0 | % | |
| 300%Strain,125°C,168hr | ASTM D573 | -15 | % | |
| 125°C,336hr | ASTM D573 | -23 | % | |
| 空气中硬度(Shore)的变化率 | ShoreD,125°C,336hr | ASTM D573 | -5.0 | - |
| ShoreD,125°C,504hr | ASTM D573 | -4.0 | - | |
| 空气中拉伸强度的变化率 | 23°C,168hr,inReferenceFuelA(Isooctane) | ASTM D471 | -3.0 | % |
| 100%Strain,23°C,168hr,inReferenceFuelA(Isooctane) | ASTM D471 | -2.0 | % | |
| 125°C,336hr | ISO 216 | -23 | % | |
| 100%Strain125°C,336hr | ISO 216 | 8.0 | % | |
| 300%Strain125°C,336hr | ISO 216 | -27 | % | |
| 空气中硬度(Shore)的变化率 | ShoreD,100°C,336hr | ISO 216 | 0.0 | - |
| 空气中拉伸强度的变化率 | 300%Strain,23°C,70hr,inReferenceFuelA(Isooctane) | ASTM D471 | 5.0 | % |
| 300%Strain,125°C,504hr | ASTM D573 | -30 | % | |
| 100°C,70hr | ISO 216 | 3.0 | % | |
| 300%Strain100°C,504hr | ISO 216 | 1.0 | % | |
| 125°C,70hr | ISO 216 | -20 | % | |
| 100%Strain125°C,70hr | ISO 216 | 7.0 | % | |
| 23°C,70hr,甲醇 | ASTM D471 | 1.0 | % | |
| 空气中硬度(Shore)的变化率 | ShoreD,100°C,70hr | ISO 216 | -2.0 | - |
| ShoreD,100°C,168hr | ISO 216 | -1.0 | - | |
| 空气中拉伸强度的变化率 | 300%Strain125°C,70hr | ISO 216 | -23 | % |
| 125°C,168hr | ISO 216 | -11 | % | |
| 100%应变125°C,168hr | ISO 216 | -2.0 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,125°C,168hr | ASTM D573 | 0.0 | - |
| 空气中拉伸强度的变化率 | 300%Strain125°C,168hr | ISO 216 | -15 | % |
| 300%Strain,23°C,70hr,inReferenceFuelC | ASTM D471 | -22 | % | |
| 空气中硬度(Shore)的变化率 | ShoreD,100°C,168hr | ASTM D573 | -1.0 | - |
| ShoreD,100°C,336hr | ASTM D573 | 0.0 | - | |
| ShoreD,100°C,504hr | ASTM D573 | 0.0 | - | |
| 空气中拉伸强度的变化率 | 100%Strain,23°C,70hr,inReferenceFuelC | ASTM D471 | -19 | % |
| 空气中硬度(Shore)的变化率 | ShoreD,125°C,70hr | ASTM D573 | 1.0 | - |
| 空气中拉伸强度的变化率 | 100°C,70hr,在ASTM#3油中 | ASTM D471 | 19 | % |
| 300%Strain,23°C,168hr,inReferenceFuelA(Isooctane) | ASTM D471 | -11 | % | |
| 23°C,168hr,甲醇 | ASTM D471 | -4.0 | % | |
| 100%Strain,23°C,168hr,inReferenceFuelC | ASTM D471 | -27 | % | |
| 300%Strain,23°C,168hr,inReferenceFuelC | ASTM D471 | -34 | % | |
| 100%Strain,100°C,70hr,inASTM#3Oil | ASTM D471 | 16 | % | |
| 300%Strain,100°C,70hr,inASTM#3Oil | ASTM D471 | 13 | % | |
| 100°C,168hr,inASTM#1Oil | ASTM D471 | -4.0 | % | |
| 23°C,336hr,inReferenceFuelA(Isooctane) | ASTM D471 | 6.0 | % | |
| 100%Strain,23°C,336hr,inReferenceFuelA(Isooctane) | ASTM D471 | 3.0 | % | |
| 300%Strain,23°C,336hr,inReferenceFuelA(Isooctane) | ASTM D471 | -1.0 | % | |
| 23°C,70hr,甲醇 | BTM 00117 | 1.0 | % | |
| 100%Strain,23°C,70hr,inReferenceFuelC | BTM 00117 | -19 | % | |
| 300%Strain,23°C,70hr,inReferenceFuelC | BTM 00117 | -22 | % | |
| 23°C,168hr,inReferenceFuelA(Isooctane) | BTM 00117 | -3.0 | % | |
| 100%Strain,23°C,168hr,inReferenceFuelA(Isooctane) | BTM 00117 | -2.0 | % | |
| 100%Strain,100°C,168hr,inASTM#1Oil | ASTM D471 | 14 | % | |
| 300%Strain,23°C,168hr,inReferenceFuelA(Isooctane) | BTM 00117 | -11 | % | |
| 23°C,168hr,甲醇 | BTM 00117 | -4.0 | % | |
| 100%Strain,23°C,168hr,inReferenceFuelC | BTM 00117 | -27 | % | |
| 300%Strain,23°C,168hr,inReferenceFuelC | BTM 00117 | -34 | % | |
| 23°C,336hr,inReferenceFuelA(Isooctane) | BTM 00117 | 6.0 | % | |
| 100%Strain,100°C,70hr,inASTM#1Oil | ASTM D471 | 12 | % | |
| 300%Strain,100°C,70hr,inASTM#1Oil | ASTM D471 | 7.0 | % | |
| 100°C,336hr,inASTM#1Oil | ASTM D471 | -20 | % | |
| 100%Strain,100°C,70hr,inASTM#1Oil | BTM 00117 | 12 | % | |
| 300%Strain,100°C,70hr,inASTM#1Oil | BTM 00117 | 7.0 | % | |
| 23°C,336hr,inReferenceFuelC | ASTM D471 | -10 | % | |
| 100%Strain,100°C,336hr,inASTM#1Oil | ASTM D471 | 14 | % | |
| 300%Strain,100°C,336hr,inASTM#1Oil | ASTM D471 | -9.0 | % | |
| 100°C,504hr,inASTM#1Oil | ASTM D471 | -29 | % | |
| 100%Strain,100°C,504hr,inASTM#1Oil | ASTM D471 | 15 | % | |
| 300%Strain,100°C,504hr,inASTM#1Oil | ASTM D471 | -14 | % | |
| 100°C,504hr,inASTM#3Oil | ASTM D471 | -18 | % | |
| 100%Strain,100°C,504hr,inASTM#3Oil | ASTM D471 | 2.0 | % | |
| 300%Strain,100°C,504hr,inASTM#3Oil | ASTM D471 | -12 | % | |
| 23°C,70hr,inReferenceFuelA(Isooctane) | BTM 00117 | 6.0 | % | |
| 100%Strain,23°C,70hr,inReferenceFuelA(Isooctane) | BTM 00117 | 2.0 | % | |
| 300%Strain,23°C,70hr,inReferenceFuelA(Isooctane) | BTM 00117 | 5.0 | % | |
| 100%Strain,23°C,336hr,inReferenceFuelA(Isooctane) | BTM 00117 | 3.0 | % | |
| 300%Strain,23°C,336hr,inReferenceFuelA(Isooctane) | BTM 00117 | -1.0 | % | |
| 23°C,336hr,inReferenceFuelC | BTM 00117 | -10 | % | |
| 100%Strain,23°C,336hr,inReferenceFuelC | BTM 00117 | -32 | % | |
| 300%Strain,23°C,336hr,inReferenceFuelC | BTM 00117 | -35 | % | |
| 23°C,504hr,inReferenceFuelA(Isooctane) | BTM 00117 | -1.0 | % | |
| 100%Strain,23°C,504hr,inReferenceFuelA(Isooctane) | BTM 00117 | 5.0 | % | |
| 300%Strain,23°C,504hr,inReferenceFuelA(Isooctane) | BTM 00117 | 3.0 | % | |
| 23°C,504hr,inReferenceFuelC | BTM 00117 | -11 | % | |
| 100%Strain,23°C,504hr,inReferenceFuelC | BTM 00117 | -27 | % | |
| 300%Strain,100°C,168hr,inASTM#1Oil | ASTM D471 | 2.0 | % | |
| 300%Strain,23°C,504hr,inReferenceFuelC | BTM 00117 | -28 | % | |
| 100°C,70hr,在ASTM#1油中 | BTM 00117 | 18 | % | |
| 100%Strain,23°C,336hr,inReferenceFuelC | ASTM D471 | -32 | % | |
| 300%Strain,23°C,336hr,inReferenceFuelC | ASTM D471 | -35 | % | |
| 23°C,504hr,inReferenceFuelA(Isooctane) | ASTM D471 | -1.0 | % | |
| 100%Strain,23°C,504hr,inReferenceFuelA(Isooctane) | ASTM D471 | 5.0 | % | |
| 300%Strain,23°C,504hr,inReferenceFuelA(Isooctane) | ASTM D471 | 3.0 | % | |
| 23°C,504hr,inReferenceFuelC | ASTM D471 | -11 | % | |
| 100%Strain,23°C,504hr,inReferenceFuelC | ASTM D471 | -27 | % | |
| 300%Strain,23°C,504hr,inReferenceFuelC | ASTM D471 | -28 | % | |
| 100°C,70hr,在ASTM#1油中 | ASTM D471 | 18 | % | |
| 100°C,336hr,inASTM#1Oil | BTM 00117 | -20 | % | |
| 100°C,70hr,在ASTM#3油中 | BTM 00117 | 19 | % | |
| 100%Strain,100°C,70hr,inASTM#3Oil | BTM 00117 | 16 | % | |
| 100%Strain,100°C,168hr,inASTM#1Oil | BTM 00117 | 14 | % | |
| 300%Strain,100°C,168hr,inASTM#1Oil | BTM 00117 | 2.0 | % | |
| 拉伸应力变化率 | 100°C,70hr,在ASTM#1油中，断裂 | BTM 00117 | 8.0 | % |
| 100°C,70hr,在ASTM#3油中，断裂 | BTM 00117 | 6.0 | % | |
| 100°C,168hr,inASTM#1Oil，断裂 | BTM 00117 | 12 | % | |
| 100°C,336hr,inASTM#1Oil，断裂 | BTM 00117 | 24 | % | |
| 空气中拉伸强度的变化率 | 300%Strain,100°C,70hr,inASTM#3Oil | BTM 00117 | 13 | % |
| 100°C,168hr,inASTM#1Oil | BTM 00117 | -4.0 | % | |
| 拉伸应力变化率 | 100°C,504hr,inASTM#1Oil，断裂 | BTM 00117 | 16 | % |
| 100°C,504hr,inASTM#3Oil，断裂 | BTM 00117 | 20 | % | |
| 空气中硬度(Shore)的变化率 | ShoreD,23°C,70hr,inReferenceFuelA(Isooctane) | ASTM D471 | -4.0 | - |
| ShoreD,23°C,70hr,inReferenceFuelC | ASTM D471 | -7.0 | - | |
| ShoreD,23°C,168hr,inReferenceFuelA(Isooctane) | ASTM D471 | 1.0 | - | |
| ShoreD,23°C,168hr,inReferenceFuelC | ASTM D471 | -4.0 | - | |
| 硬度 | ShoreD,23°C,70hr,inReferenceFuelA(Isooctane) | BTM 00117 | -4.0 | - |
| ShoreD,23°C,70hr,inReferenceFuelC | BTM 00117 | -7.0 | - | |
| ShoreD,23°C,168hr,inReferenceFuelA(Isooctane) | BTM 00117 | 1.0 | - | |
| ShoreD,23°C,168hr,inReferenceFuelC | BTM 00117 | -4.0 | - | |
| ShoreD,23°C,336hr,inReferenceFuelA(Isooctane) | BTM 00117 | -1.0 | - | |
| ShoreD,23°C,336hr,inReferenceFuelC | BTM 00117 | -6.0 | - | |
| ShoreD,23°C,504hr,inReferenceFuelA(Isooctane) | BTM 00117 | 6.0 | - | |
| ShoreD,23°C,504hr,inReferenceFuelC | BTM 00117 | -8.0 | - | |
| ShoreD,100°C,70hr,inASTM#1Oil | BTM 00117 | 2.0 | - | |
| ShoreD,100°C,70hr,inASTM#3Oil | BTM 00117 | 2.0 | - | |
| 空气中拉伸强度的变化率 | 300%Strain,100°C,504hr,inASTM#1Oil | BTM 00117 | -14 | % |
| 100°C,504hr,inASTM#3Oil | BTM 00117 | -18 | % | |
| 100%Strain,100°C,504hr,inASTM#3Oil | BTM 00117 | 2.0 | % | |
| 300%Strain,100°C,504hr,inASTM#3Oil | BTM 00117 | -12 | % | |
| 空气中极限伸长率的变化率 | 100°C,504hr,inASTM#1Oil | ASTM D471 | 16 | % |
| 拉伸应力变化率 | 23°C,336hr,inReferenceFuelC，断裂 | BTM 00117 | -2.0 | % |
| 23°C,504hr,inReferenceFuelA(Isooctane)，断裂 | BTM 00117 | -2.0 | % | |
| 空气中极限伸长率的变化率 | 100°C,504hr,inASTM#3Oil | ASTM D471 | 20 | % |
| 拉伸应力变化率 | 23°C,70hr,inReferenceFuelA(Isooctane)，断裂 | BTM 00117 | -4.0 | % |
| 23°C,70hr,甲醇，断裂 | BTM 00117 | 5.0 | % | |
| 23°C,168hr,inReferenceFuelA(Isooctane)，断裂 | BTM 00117 | 9.0 | % | |
| 23°C,168hr,甲醇，断裂 | BTM 00117 | 6.0 | % | |
| 23°C,336hr,inReferenceFuelA(Isooctane)，断裂 | BTM 00117 | -4.0 | % | |
| 23°C,504hr,inReferenceFuelC，断裂 | BTM 00117 | -8.0 | % | |
| 空气中拉伸强度的变化率 | 100%Strain,100°C,336hr,inASTM#1Oil | BTM 00117 | 14 | % |
| 300%Strain,100°C,336hr,inASTM#1Oil | BTM 00117 | -9.0 | % | |
| 100°C,504hr,inASTM#1Oil | BTM 00117 | -29 | % | |
| 100%Strain,100°C,504hr,inASTM#1Oil | BTM 00117 | 15 | % | |
| 空气中极限伸长率的变化率 | 23°C,504hr,inReferenceFuelC | ASTM D471 | -8.0 | % |
| 23°C,70hr,inReferenceFuelA(Isooctane) | ASTM D471 | -4.0 | % | |
| 23°C,70hr,甲醇 | ASTM D471 | 5.0 | % | |
| 23°C,168hr,inReferenceFuelA(Isooctane) | ASTM D471 | 9.0 | % | |
| 23°C,168hr,甲醇 | ASTM D471 | 6.0 | % | |
| 23°C,336hr,inReferenceFuelA(Isooctane) | ASTM D471 | -4.0 | % | |
| 23°C,336hr,inReferenceFuelC | ASTM D471 | -2.0 | % | |
| 23°C,504hr,inReferenceFuelA(Isooctane) | ASTM D471 | -2.0 | % | |
| 体积变化 | 23°C,336hr,inReferenceFuelC | BTM 00117 | 14 | % |
| 空气中极限伸长率的变化率 | 100°C,70hr,在ASTM#1油中 | ASTM D471 | 8.0 | % |
| 100°C,70hr,在ASTM#3油中 | ASTM D471 | 6.0 | % | |
| 100°C,168hr,inASTM#1Oil | ASTM D471 | 12 | % | |
| 体积变化 | 23°C,504hr,inReferenceFuelA | BTM 00117 | 0.0 | % |
| 空气中极限伸长率的变化率 | 100°C,336hr,inASTM#1Oil | ASTM D471 | 24 | % |
| 空气中硬度(Shore)的变化率 | ShoreD,23°C,336hr,inReferenceFuelA(Isooctane) | ASTM D471 | -1.0 | - |
| ShoreD,23°C,336hr,inReferenceFuelC | ASTM D471 | -6.0 | - | |
| ShoreD,23°C,504hr,inReferenceFuelA(Isooctane) | ASTM D471 | 6.0 | - | |
| ShoreD,23°C,504hr,inReferenceFuelC | ASTM D471 | -8.0 | - | |
| ShoreD,100°C,70hr,inASTM#1Oil | ASTM D471 | 2.0 | - | |
| ShoreD,100°C,70hr,inASTM#3Oil | ASTM D471 | 2.0 | - | |
| ShoreD,100°C,168hr,inASTM#1Oil | ASTM D471 | 1.0 | - | |
| ShoreD,100°C,336hr,inASTM#1Oil | ASTM D471 | -2.0 | - | |
| ShoreD,100°C,504hr,inASTM#1Oil | ASTM D471 | 0.0 | - | |
| ShoreD,100°C,504hr,inASTM#3Oil | ASTM D471 | -1.0 | - | |
| 体积变化 | 23°C,168hr,inReferenceFuelA | BTM 00117 | 0.0 | % |
| 23°C,168hr,甲醇 | BTM 00117 | 10 | % | |
| 23°C,336hr,inReferenceFuelA | BTM 00117 | 0.0 | % | |
| 23°C,504hr,inReferenceFuelC | BTM 00117 | 14 | % | |
| 100°C,70hr,在ASTM#1油中 | BTM 00117 | -1.0 | % | |
| 100°C,70hr,在ASTM#3油中 | BTM 00117 | 2.0 | % | |
| 100°C,168hr,inASTM#1Oil | BTM 00117 | 0.0 | % | |
| 100°C,336hr,inASTM#1Oil | BTM 00117 | -1.0 | % | |
| 23°C,504hr,inReferenceFuelA | ASTM D471 | 0.0 | % | |
| 23°C,504hr,inReferenceFuelC | ASTM D471 | 14 | % | |
| 100°C,70hr,在ASTM#1油中 | ASTM D471 | -1.0 | % | |
| 100°C,70hr,在ASTM#3油中 | ASTM D471 | 2.0 | % | |
| 100°C,168hr,inASTM#1Oil | ASTM D471 | 0.0 | % | |
| 100°C,336hr,inASTM#1Oil | ASTM D471 | -1.0 | % | |
| 23°C,336hr,inReferenceFuelC | ASTM D471 | 14 | % | |
| 100°C,504hr,inASTM#1Oil | BTM 00117 | -1.0 | % | |
| 100°C,504hr,inASTM#3Oil | BTM 00117 | 4.0 | % | |
| 100°C,504hr,inASTM#1Oil | ASTM D471 | -1.0 | % | |
| 100°C,504hr,inASTM#3Oil | ASTM D471 | 4.0 | % | |
| 23°C,70hr,inReferenceFuelA | BTM 00117 | 0.0 | % | |
| 23°C,70hr,甲醇 | BTM 00117 | 6.0 | % | |
| 硬度 | ShoreD,100°C,168hr,inASTM#1Oil | BTM 00117 | 1.0 | - |
| ShoreD,100°C,336hr,inASTM#1Oil | BTM 00117 | -2.0 | - | |
| ShoreD,100°C,504hr,inASTM#1Oil | BTM 00117 | 0.0 | - | |
| ShoreD,100°C,504hr,inASTM#3Oil | BTM 00117 | -1.0 | - | |
| 体积变化 | 23°C,70hr,inReferenceFuelA | ASTM D471 | 0.0 | % |
| 23°C,70hr,甲醇 | ASTM D471 | 6.0 | % | |
| 23°C,168hr,inReferenceFuelA | ASTM D471 | 0.0 | % | |
| 23°C,168hr,甲醇 | ASTM D471 | 10 | % | |
| 23°C,336hr,inReferenceFuelA | ASTM D471 | 0.0 | % |
【免责声明】
普拉司网尽最大努力确保此数据的准确性，但是普拉司网对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。
认证信息
暂无认证数据
替代型号推荐
暂无替代型号推荐
该产品暂时没有可推荐的替代型号