完善物性
TPU Generic TPU, Unspecified Generic
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 密度 | -- | ASTM D792 | 0.978to1.43 | g/cm³ |
| 23°C | ISO 1183 | 0.938to1.22 | g/cm³ | |
| 熔体质量流动速率 | 230°C/2.16kg | ISO 1133 | 0.80to5.0 | g/10min |
| 收缩率 | MD：23°C | ASTM D955 | 0.35to3.7 | % |
| 吸水率 | 23°C,24hr | ASTM D570 | 0.020to0.30 | % |
| 密度 | -- | ASTM D792 | 0.978to1.43 | g/cm³ |
| 23°C | ISO 1183 | 0.938to1.22 | g/cm³ | |
| 熔体质量流动速率 | 230°C/2.16kg | ISO 1133 | 0.80to5.0 | g/10min |
| 收缩率 | MD：23°C | ASTM D955 | 0.35to3.7 | % |
| 吸水率 | 23°C,24hr | ASTM D570 | 0.020to0.30 | % |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸强度 | 23°C | ASTM D638 | 1.31to12.9 | MPa |
| 23°C | ISO 527-2 | 2.00to32.2 | MPa | |
| 23°C | ASTM D1708 | 2.47to16.1 | MPa | |
| 伸长率 | 断裂,23°C | ASTM D638 | 20to580 | % |
| 断裂,23°C | ISO 527-2 | 430to1100 | % | |
| 弯曲模量 | 23°C | ASTM D790 | 22.1to79.9 | MPa |
| 弯曲强度 | 23°C | ASTM D790 | 1.45to83.0 | MPa |
| 泰伯耐磨性 | 23°C | ASTM D1044 | 5.40to85.1 | mg |
| 拉伸强度 | 断裂,23°C | ASTM D638 | 4.14to65.5 | MPa |
| 断裂,23°C | ISO 527-2 | 18.3to50.0 | MPa | |
| 23°C | ASTM D638 | 1.31to12.9 | MPa | |
| 23°C | ISO 527-2 | 2.00to32.2 | MPa | |
| 23°C | ASTM D1708 | 2.47to16.1 | MPa | |
| 伸长率 | 断裂,23°C | ASTM D638 | 20to580 | % |
| 断裂,23°C | ISO 527-2 | 430to1100 | % | |
| 弯曲模量 | 23°C | ASTM D790 | 22.1to79.9 | MPa |
| 弯曲强度 | 23°C | ASTM D790 | 1.45to83.0 | MPa |
| 拉伸强度 | 断裂,23°C | ASTM D638 | 4.14to65.5 | MPa |
| 断裂,23°C | ISO 527-2 | 18.3to50.0 | MPa | |
| 拉伸模量 | 23°C | ASTM D638 | 1450to2330 | MPa |
| 拉伸强度 | 屈服,23°C | ASTM D638 | 8.27to76.5 | MPa |
| 拉伸模量 | 23°C | ASTM D638 | 1450to2330 | MPa |
| 拉伸强度 | 屈服,23°C | ASTM D638 | 8.27to76.5 | MPa |
| 泰伯耐磨性 | 23°C | ASTM D1044 | 5.40to85.1 | mg |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 热变形温度 | 1.8MPa,未退火 | ASTM D648 | 71.9to79.4 | °C |
| 玻璃转化温度 | - | ASTME1356 | -67.0-79.0 | °C |
| 维卡软化温度 | - | ASTM D1525 | 66.7to105 | °C |
| 热变形温度 | 1.8MPa,未退火 | ASTM D648 | 71.9to79.4 | °C |
| 玻璃转化温度 | - | ASTME1356 | -67.0-79.0 | °C |
| 维卡软化温度 | - | ASTM D1525 | 66.7to105 | °C |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸强度 | 屈服,23°C | ASTM D412 | 2.50to25.2 | MPa |
| 屈服,23°C | ISO 37 | 13.8to30.4 | MPa | |
| 断裂,23°C | ASTM D412 | 6.00to41.1 | MPa | |
| 伸长率 | 断裂,23°C | ASTM D412 | 190to1200 | % |
| 断裂,23°C | ISO 37 | 450to980 | % | |
| 撕裂强度 | 23°C | ASTM D624 | 19.3to136 | kN/m |
| 拉伸强度 | 100%应变,23°C | ISO 37 | 0.900to16.0 | MPa |
| 300%应变,23°C | ASTM D412 | 2.07to29.6 | MPa | |
| 300%应变,23°C | ISO 37 | 9.00to25.3 | MPa | |
| 撕裂强度 | 23°C | ISO 34-1 | 26to150 | kN/m |
| 压缩永久变形 | -- | ASTM D395 | 13to70 | % |
| 23°C | ISO 815 | 18to53 | % | |
| 拉伸强度 | 100%应变,23°C | ASTM D412 | 0.827to7.01 | MPa |
| 100%应变,23°C | ISO 37 | 0.900to16.0 | MPa | |
| 300%应变,23°C | ASTM D412 | 2.07to29.6 | MPa | |
| 300%应变,23°C | ISO 37 | 9.00to25.3 | MPa | |
| 屈服,23°C | ASTM D412 | 2.50to25.2 | MPa | |
| 屈服,23°C | ISO 37 | 13.8to30.4 | MPa | |
| 断裂,23°C | ASTM D412 | 6.00to41.1 | MPa | |
| 伸长率 | 断裂,23°C | ASTM D412 | 190to1200 | % |
| 断裂,23°C | ISO 37 | 450to980 | % | |
| 撕裂强度 | 23°C | ASTM D624 | 19.3to136 | kN/m |
| 23°C | ISO 34-1 | 26to150 | kN/m | |
| 压缩永久变形 | -- | ASTM D395 | 13to70 | % |
| 23°C | ISO 815 | 18to53 | % | |
| 拉伸强度 | 100%应变,23°C | ASTM D412 | 0.827to7.01 | MPa |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 洛氏硬度 | 23°C | ASTM D785 | 50to110 | - |
| 硬度 | 23°C | ASTM D2240 | 40to95 | - |
| 23°C | ISO 868 | 40to97 | - | |
| 23°C | ASTM D2240 | 40to95 | - | |
| 23°C | ISO 868 | 40to97 | - | |
| 洛氏硬度 | 23°C | ASTM D785 | 50to110 | - |
| 冲击性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 悬臂梁缺口冲击强度 | 23°C | ASTM D256 | 260to870 | J/m |
| 23°C | ASTM D256 | 260to870 | J/m |