TPU-Ether Generic TPU-Polyether Generic
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 密度 | -- | ASTM D792 | 1.10to1.17 | g/cm³ |
| 23°C | ISO 1183 | 1.06to1.21 | g/cm³ | |
| -- | ISO 11831 | 1110 | kg/m³ | |
| -- | ASTM D1505 | 0.300to1.05 | g/cm³ | |
| 熔体质量流动速率 | 190°C/8.7kg | ASTM D1238 | 14to24 | g/10min |
| 收缩率 | MD:23°C | ASTM D955 | 0.63to0.90 | % |
| TD:23°C | ASTM D955 | 0.80to0.82 | % | |
| 23°C | ISO 294-4 | 0.80to0.81 | % | |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸模量 | 23°C | ISO 527-2 | 90.0to808 | MPa |
| 拉伸强度 | 断裂,23°C | ISO 527-2 | 25.0to53.1 | MPa |
| 23°C | ASTM D638 | 1.00to44.1 | MPa | |
| 23°C | ISO 527-2 | 1.00to35.2 | MPa | |
| 伸长率 | 断裂,23°C | ASTM D638 | 340to610 | % |
| 断裂,23°C | ISO 527-2 | 340to800 | % | |
| 弯曲模量 | 23°C | ASTM D790 | 4.83to121 | MPa |
| 23°C | ISO 178 | 18.6to193 | MPa | |
| 泰伯耐磨性 | 23°C | ASTM D1044 | 3.00to78.9 | mg |
| 拉伸模量 | 23°C | ASTM D638 | 5.52to63.6 | MPa |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 雾度 | - | ASTM D1003 | 0.15to3.0 | % |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 玻璃转化温度 | -- | DSC | -60.7--26.3 | °C |
| 维卡软化温度 | -- | ASTM D1525 | 66.7to145 | °C |
| -- | ISO 306 | 75.0to139 | °C | |
| 熔融温度 | -- | - | 175to205 | °C |
| -- | DSC | 134to176 | °C | |
| 线性热膨胀系数 | MD | ASTM D696 | 1.3E-4到1.7E-4 | cm/cm/°C |
| 脆化温度 | - | ASTM D746 | -68.6--35.8 | °C |
| 玻璃转化温度 | -- | ASTME1356 | -48.4--13.5 | °C |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 拉伸强度 | 20%应变,23°C | ISO 37 | 1.99to16.5 | MPa |
| 50%应变,23°C | ASTM D412 | 1.10to12.3 | MPa | |
| 100%应变,23°C | ASTM D412 | 2.42to17.6 | MPa | |
| 100%应变,23°C | ISO 37 | 2.78to25.3 | MPa | |
| 300%应变,23°C | ASTM D412 | 4.94to36.6 | MPa | |
| 300%应变,23°C | ISO 37 | 4.80to45.0 | MPa | |
| 屈服,23°C | ASTM D412 | 14.7to44.0 | MPa | |
| 屈服,23°C | ISO 37 | 29.5to50.7 | MPa | |
| 断裂,23°C | ASTM D412 | 23.4to56.3 | MPa | |
| 断裂,23°C | ISO 37 | 25.3to51.7 | MPa | |
| 23°C | ASTM D412 | 24.4to50.3 | MPa | |
| 伸长率 | 断裂,23°C | ASTM D412 | 350to780 | % |
| 断裂,23°C | ISO 37 | 350to760 | % | |
| 断裂 | ASTM D412 | 55 | % | |
| 拉伸永久变形 | 23°C | ASTM D412 | 6to21 | % |
| 硬度 | - | ASTM D2632 | 35to51 | % |
| 撕裂强度 | 23°C | ASTM D624 | 47.6to167 | kN/m |
| 开裂 | ASTM D470 | 29 | kN/m | |
| 23°C | ISO 34-1 | 39to190 | kN/m | |
| 压缩永久变形 | -- | ASTM D395 | 19to47 | % |
| 23°C | ISO 815 | 20to40 | % | |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 硬度 | 23°C | ASTM D2240 | 50to96 | - |
| 23°C | ISO 868 | 34to98 | - | |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 水蒸气透过率 | - | ASTME96 | 400to9100 | g/m²/24hr |
| 老化 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 空气中拉伸强度的变化率 | 23°C | ASTM D471 | -28-13 | % |
| 体积变化 | 23°C | ASTM D471 | 0.50to36 | % |