完善物性
ULDPE 4404G 美国陶氏
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
典型应用：
主要用于包装
特性：
高的韧性和光学性能,通过加拿大HPFB认证
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 密度 | - | ASTM D792 | 0.904 | g/cm³ |
| 熔体质量流动速率 | 190°C/2.16kg | ASTM D1238 | 4.0 | g/10min |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 断裂伸长率 | MD | ASTM D-882 | 664 | % |
| 拉伸模量 | TD | ASTM D-882 | 63 | MPa |
| MD | ASTM D-882 | 63 | MPa | |
| 穿刺强度 | - | 陶氏企业测试 | 17 | J/cm3 |
| 拉伸强度 | 屈服,TD | ASTM D-882 | 5 | MPa |
| 屈服,MD | ASTM D-882 | 7 | MPa | |
| TD，断裂 | ASTM D-882 | 32 | MPa | |
| MD，断裂 | ASTM D-882 | 33 | MPa | |
| 断裂伸长率 | TD | ASTM D-882 | 714 | % |
| 光学性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 透明度 | - | ASTM D-1746 | 99 | - |
| 光泽度 | 45° | ASTM D-2457 | 90 | - |
| 雾度 | - | ASTM D-1003 | 1.8 | % |
| 光泽度 | 45°,20.3µm | ASTM D2457 | 92 | - |
| 45°,50.8µm | ASTM D2457 | 90 | - | |
| 透明度 | 20.3µm | ASTM D1746 | 99.0 | - |
| 50.8µm | ASTM D1746 | 99.0 | - | |
| 雾度 | 20.3µm | ASTM D1003 | 0.60 | % |
| 50.8µm | ASTM D1003 | 1.8 | % | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 维卡软化温度 | - | ASTM D1525 | 71.1 | °C |
| 熔融温度 | - | Internal Method | 124 | °C |
| 维卡软化温度 | - | ASTM D-1525 | 71 | ℃ |
| 基本性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 熔体质量流动速率 | - | ASTM D1238 | 4 | g/10min |
| 密度 | - | ASTM D792 | 0.904 | g/cm3 |
| 薄膜 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 薄膜穿刺强度 | 20µm | Internal Method | 18.9 | J/cm³ |
| 51µm | Internal Method | 17.5 | J/cm³ | |
| 割线模量 | 2%正割,MD:20µm | ASTM D882 | 58.8 | MPa |
| 2%正割,MD:51µm | ASTM D882 | 62.6 | MPa | |
| 2%正割,TD:20µm | ASTM D882 | 64.7 | MPa | |
| 2%正割,TD:51µm | ASTM D882 | 63.0 | MPa | |
| 拉伸强度 | MD:屈服,20µm | ASTM D882 | 7.00 | MPa |
| MD:屈服,51µm | ASTM D882 | 6.76 | MPa | |
| TD:屈服,20µm | ASTM D882 | 4.92 | MPa | |
| TD:屈服,51µm | ASTM D882 | 6.34 | MPa | |
| MD:断裂,20µm | ASTM D882 | 36.9 | MPa | |
| MD:断裂,51µm | ASTM D882 | 32.6 | MPa | |
| TD:断裂,20µm | ASTM D882 | 29.1 | MPa | |
| TD:断裂,51µm | ASTM D882 | 32.4 | MPa | |
| 伸长率 | TD:断裂,51µm | ASTM D882 | 710 | % |
| 落镖冲击 | 20µm | ASTM D1709B | >850 | g |
| 51µm | ASTM D1709B | >850 | g | |
| 埃尔曼多夫撕裂强度 | MD:20µm | ASTM D1922 | 330 | g |
| MD:51µm | ASTM D1922 | 960 | g | |
| 伸长率 | MD:断裂,20µm | ASTM D882 | 500 | % |
| MD:断裂,51µm | ASTM D882 | 660 | % | |
| TD:断裂,20µm | ASTM D882 | 710 | % | |
| 埃尔曼多夫撕裂强度 | TD:20µm | ASTM D1922 | 500 | g |
| TD:51µm | ASTM D1922 | 1100 | g | |
| 氧气透过率 | 23°C,51µm | ASTM D3985 | 450 | cm³·mm/m²/atm/24hr |
| 水蒸气透过率 | 51µm | ASTMF1249 | 0.85 | g·mm/m²/atm/24hr |
| 二氧化碳透过率 | 23°C,50.8µm | Internal Method | 2000 | cm³·mm/m²/atm/24hr |
【免责声明】
普拉司网尽最大努力确保此数据的准确性，但是普拉司网对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。
认证信息
暂无认证数据
替代型号推荐
暂无替代型号推荐
该产品暂时没有可推荐的替代型号