Ethylene Copolymer Orevac® T 9307 Y 法国阿科玛
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
特性：
机械性能
物性表
| 测试条件 | 测试方法 | 测试结果 | 测试单位 | |
|---|---|---|---|---|
| 拉伸应变 | Break,2.80mm,CompressionMolded | ASTM D638 | 700to900 | % |
| Break,2.80mm,CompressionMolded | ISO 527-2/5A/50 | 700to900 | % | |
| DurometerHardness | ShoreA,15sec,2.80mm,CompressionMolded | ASTM D2240 | 91 | - |
| 硬度 | ShoreA,15sec,2.80mm,CompressionMolded | ISO 868 | 91 | - |
| 维卡软化温度 | - | ASTM D15253 | 66.0 | °C |
| - | ISO 306/A | 66.0 | °C | |
| 熔融温度 | - | ISO 11357-3 | 93.0 | °C |
| RingandBallSofteningPoint | - | ASTME28 | 145 | °C |
| 密度 | - | ASTM D1505 | 0.939 | g/cm³ |
| - | ISO 1183 | 0.939 | g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ASTM D1238 | 9.5to12 | g/10min |
| 190°C/2.16kg | ISO 1133 | 9.5to12 | g/10min | |
| 醋酸乙烯含量 | - | - | 13.0to15.0 | wt% |
| 马来酸酐含量 | - | - | 1600 | ppm |
| 拉伸强度 | Break,2.80mm,CompressionMolded | ASTM D638 | 19.0 | MPa |
| Break,2.80mm,CompressionMolded | ISO 527-2/5A/50 | 19.0 | MPa |