TPU-Ether Texin® 950 德国科思创
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 收缩率 | MD:2.54mm | ASTM D955 | 0.80 | % |
| TD:2.54mm | ASTM D955 | 0.80 | % | |
| TD:2.54mm | ISO 2577 | 0.80 | % | |
| MD:2.54mm | ISO 2577 | 0.80 | % | |
| 密度 | - | ASTMD792 | 1.15 | g/cm³ |
| 机械性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 弯曲模量 | 23°C | ASTMD790 | 114 | MPa |
| 70°C | ASTMD790 | 46.9 | MPa | |
| 泰伯耐磨性 | 1000Cycles,1000g,H-18转轮 | ASTM D1044 | 75.0 | mg |
| 1000Cycles,1000g,H-18转轮 | ISO 4649 | 75.0 | mg | |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 脆化温度 | - | ASTMD746 | <-68.0 | °C |
| 玻璃转化温度 | - | DMA | -27.0 | °C |
| 维卡软化温度 | - | ISO 306/50 | 128 | °C |
| 线性热膨胀系数 | MD | ASTM D696 | 1.3E-04 | cm/cm/°C |
| 弹性体 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 伸长率 | 断裂 | ASTMD412 | 470 | % |
| 撕裂强度 | --2 | ASTM D624 | 131 | kN/m |
| -- | ISO 34-1 | 130 | kN/m | |
| 压缩永久变形 | 23°C,22hr | ASTMD395B | 20 | % |
| 23°C,22hr3 | ASTMD395B | 15 | % | |
| 70°C,22hr | ASTMD395B | 70 | % | |
| 70°C,22hr3 | ASTMD395B | 40 | % | |
| 硬度 | - | ASTM D2632 | 35 | % |
| 拉伸强度 | 50%应变 | ASTMD412 | 12.1 | MPa |
| 100%应变 | ASTMD412 | 13.8 | MPa | |
| 300%应变 | ASTMD412 | 27.6 | MPa | |
| 屈服 | ASTMD412 | 49.0 | MPa | |
| 硬度 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 硬度 | 邵氏D | ASTMD2240 | 50 | - |
| 补充信息 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| CompressiveLoad | 5%Deflection | ASTM D575 | 2.93 | MPa |
| 50%Deflection | ASTM D575 | 31.0 | MPa | |
| 10%Deflection | ASTM D575 | 5.52 | MPa | |
| 15%Deflection | ASTM D575 | 7.58 | MPa | |
| 2%Deflection | ASTM D575 | 1.03 | MPa | |
| 20%Deflection | ASTM D575 | 10.3 | MPa | |
| 25%Deflection | ASTM D575 | 12.4 | MPa | |
| 老化 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 空气中拉伸强度的变化率 | 100%应变,100°C,70hr,在ASTM#3油中 | ISO 175 | 2.0 | % |
| 300%应变,100°C,70hr,在ASTM#3油中 | ISO 175 | 3.0 | % | |
| 100°C,168hr,在ASTM#3油中 | ISO 175 | 12 | % | |
| 100%应变,100°C,168hr,在ASTM#3油中 | ISO 175 | -7.0 | % | |
| 100°C,504hr,在ASTM#3油中 | ASTM D471 | 1.0 | % | |
| 100%应变,100°C,504hr,在ASTM#3油中 | ASTM D471 | -9.0 | % | |
| 300%应变,100°C,504hr,在ASTM#3油中 | ASTM D471 | -18 | % | |
| 23°C,70hr,inReferenceFuelC | ISO 175 | -17 | % | |
| 100%应变,23°C,70hr,inReferenceFuelC | ISO 175 | -42 | % | |
| 300%应变,23°C,70hr,inReferenceFuelC | ISO 175 | -36 | % | |
| 100°C,168hr | ASTMD573 | 2.0 | % | |
| 100%应变,100°C,168hr | ASTM D573 | 4.0 | % | |
| 300%应变,100°C,168hr | ASTM D573 | -1.0 | % | |
| 100°C,336hr | ASTMD573 | 4.0 | % | |
| 23°C,504hr,在基准燃料A中 | ASTM D471 | 13 | % | |
| 100%应变,23°C,504hr,在基准燃料A中 | ASTM D471 | -4.0 | % | |
| 300%应变,23°C,504hr,在基准燃料A中 | ASTM D471 | -4.0 | % | |
| 100°C,70hr,在ASTM#1油中 | ASTMD471 | 2.0 | % | |
| 100%应变,100°C,70hr,在ASTM#1油中 | ASTMD471 | 7.0 | % | |
| 300%应变,100°C,70hr,在ASTM#1油中 | ASTMD471 | 4.0 | % | |
| 100°C,70hr,在ASTM#3油中 | ASTM D471 | 10 | % | |
| 100%应变,100°C,70hr,在ASTM#3油中 | ASTM D471 | 2.0 | % | |
| 100%应变,23°C,70hr,在参考燃料A中（异辛烷） | ISO 175 | -3.0 | % | |
| 300%应变,23°C,70hr,在参考燃料A中（异辛烷） | ISO 175 | 0.0 | % | |
| 23°C,168hr,inReferenceFuelC | ISO 175 | -17 | % | |
| 100%应变,23°C,168hr,inReferenceFuelC | ISO 175 | -36 | % | |
| 300%应变,23°C,168hr,inReferenceFuelC | ISO 175 | -30 | % | |
| 23°C,168hr,在参考燃料A中（异辛烷） | ISO 175 | 16 | % | |
| 100%应变,23°C,168hr,在参考燃料A中（异辛烷） | ISO 175 | 6.0 | % | |
| 300%应变,23°C,168hr,在参考燃料A中（异辛烷） | ISO 175 | 2.0 | % | |
| 23°C,336hr,inReferenceFuelC | ISO 175 | -20 | % | |
| 300%应变,23°C,168hr,在基准燃料A中 | ASTM D471 | 2.0 | % | |
| 23°C,336hr,C级标准燃料 | ASTM D471 | -20 | % | |
| 100%应变,23°C,336hr,C级标准燃料 | ASTM D471 | -36 | % | |
| 100%应变,125°C,336hr | ASTM D573 | 0.0 | % | |
| 300%应变,125°C,336hr | ASTM D573 | -22 | % | |
| 125°C,504hr | ASTMD573 | -44 | % | |
| 100%应变,125°C,504hr | ASTM D573 | -5.0 | % | |
| 300%应变,125°C,504hr | ASTM D573 | -25 | % | |
| 100%应变100°C,70hr | ISO 216 | 4.0 | % | |
| 300%应变100°C,70hr | ISO 216 | 2.0 | % | |
| 100%应变100°C,168hr | ISO 216 | 4.0 | % | |
| 300%应变,100°C,336hr,在ASTM#3油中 | ASTM D471 | -9.0 | % | |
| 100°C,504hr,在ASTM#1油中 | ASTMD471 | -3.0 | % | |
| 100%应变,100°C,504hr,在ASTM#1油中 | ASTMD471 | 4.0 | % | |
| 300%应变,100°C,504hr,在ASTM#1油中 | ASTMD471 | -7.0 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,23°C,168hr,inReferenceFuelC | ASTMD471 | -13 | - |
| 支撐D,23°C,168hr,在基准燃料A中 | ASTM D471 | 1.0 | - | |
| 支撐D,23°C,336hr,inReferenceFuelC | ASTMD471 | -10 | - | |
| 体积变化 | 100°C,504hr,在ASTM#1油中 | ISO 175 | 0.0 | % |
| 23°C,70hr,C级标准燃料 | ASTM D471 | 22 | % | |
| 23°C,168hr,A级标准燃料 | ASTM D471 | 1.0 | % | |
| 23°C,168hr,C级标准燃料 | ASTM D471 | 26 | % | |
| 23°C,336hr,A级标准燃料 | ASTM D471 | 1.0 | % | |
| 23°C,336hr,在基准燃料C中 | ISO 175 | 26 | % | |
| 23°C,504hr,在基准燃料A中 | ISO 175 | 1.0 | % | |
| 23°C,504hr,在基准燃料C中 | ISO 175 | 26 | % | |
| 100°C,70hr,在ASTM#3油中 | ISO 175 | 9.0 | % | |
| 100°C,70hr,在ASTM#1油中 | ISO 175 | 0.0 | % | |
| 100°C,168hr,在ASTM#3油中 | ISO 175 | 10 | % | |
| 100°C,168hr,在ASTM#1油中 | ISO 175 | 0.0 | % | |
| 100°C,336hr,在ASTM#3油中 | ISO 175 | 12 | % | |
| 100°C,336hr,在ASTM#1油中 | ISO 175 | 0.0 | % | |
| 100°C,504hr,在ASTM#3油中 | ISO 175 | 13 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,100°C,504hr,在ASTM#3油中 | ASTM D471 | -2.0 | - |
| 空气中拉伸强度的变化率 | 100%应变,23°C,504hr,C级标准燃料 | ASTM D471 | -36 | % |
| 300%应变,23°C,504hr,C级标准燃料 | ASTM D471 | -51 | % | |
| 300%应变100°C,168hr | ISO 216 | -1.0 | % | |
| 100%应变100°C,336hr | ISO 216 | 4.0 | % | |
| 300%应变100°C,336hr | ISO 216 | -2.0 | % | |
| 100%应变100°C,504hr | ISO 216 | 5.0 | % | |
| 300%应变100°C,504hr | ISO 216 | -3.0 | % | |
| 100%应变125°C,70hr | ISO 216 | 1.0 | % | |
| 空气中极限伸长率的变化率 | 100°C,70hr | ASTMD573 | 10 | % |
| 100°C,168hr | ASTMD573 | 15 | % | |
| 100°C,336hr | ASTMD573 | 19 | % | |
| 100°C,504hr | ASTMD573 | 16 | % | |
| 125°C,70hr | ASTMD573 | 22 | % | |
| 125°C,168hr | ASTMD573 | 29 | % | |
| 125°C,336hr | ASTMD573 | 12 | % | |
| 空气中拉伸强度的变化率 | 100%应变,23°C,70hr,C级标准燃料 | ASTM D471 | -42 | % |
| 300%应变,23°C,70hr,C级标准燃料 | ASTM D471 | -36 | % | |
| 23°C,70hr,在基准燃料A中 | ASTM D471 | 16 | % | |
| 100%应变,23°C,70hr,在基准燃料A中 | ASTM D471 | -3.0 | % | |
| 300%应变,100°C,168hr,在ASTM#3油中 | ASTM D471 | -11 | % | |
| 100°C,336hr,在ASTM#1油中 | ASTMD471 | -2.0 | % | |
| 100%应变,100°C,336hr,在ASTM#1油中 | ASTMD471 | 8.0 | % | |
| 300%应变,100°C,336hr,在ASTM#1油中 | ASTMD471 | 0.0 | % | |
| 100°C,336hr,在ASTM#3油中 | ASTM D471 | -3.0 | % | |
| 100%应变,100°C,336hr,在ASTM#3油中 | ASTM D471 | -2.0 | % | |
| 空气中极限伸长率的变化率 | 125°C,504hr | ASTMD573 | 9.0 | % |
| 空气中硬度(Shore)的变化率 | 支撐D,100°C,70hr | ASTMD573 | -1.0 | - |
| 支撐D,100°C,168hr | ASTMD573 | 0.0 | - | |
| 支撐D,100°C,336hr | ASTMD573 | -2.0 | - | |
| 支撐D,100°C,504hr | ASTMD573 | -1.0 | - | |
| 支撐D,125°C,70hr | ASTMD573 | 1.0 | - | |
| 支撐D,100°C,504hr,在ASTM#1油中 | ASTMD471 | 2.0 | - | |
| 空气中极限伸长率的变化率 | 100°C,336hr,在ASTM#3油中 | ASTM D471 | 27 | % |
| 100°C,504hr,在ASTM#1油中 | ASTMD471 | 32 | % | |
| 100°C,504hr,在ASTM#3油中 | ASTM D471 | 38 | % | |
| 23°C,70hr,inReferenceFuelC | ISO 175 | 0.0 | % | |
| 23°C,70hr,在参考燃料A中（异辛烷） | ISO 175 | 5.0 | % | |
| 23°C,168hr,inReferenceFuelC | ISO 175 | -6.0 | % | |
| 23°C,168hr,在参考燃料A中（异辛烷） | ISO 175 | 7.0 | % | |
| 23°C,168hr,在基准燃料A中 | ASTM D471 | 7.0 | % | |
| 23°C,336hr,C级标准燃料 | ASTM D471 | -5.0 | % | |
| 23°C,336hr,在基准燃料A中 | ASTM D471 | 3.0 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,23°C,70hr,inReferenceFuelC | ASTMD471 | -11 | - |
| 支撐D,23°C,70hr,在基准燃料A中 | ASTM D471 | 1.0 | - | |
| 支撐D,100°C,70hr,在ASTM#3油中 | ISO 175 | 5.0 | - | |
| 支撐D,100°C,168hr,在ASTM#3油中 | ISO 175 | 5.0 | - | |
| 支撐D,100°C,336hr,在ASTM#3油中 | ISO 175 | -4.0 | - | |
| 支撐D,100°C,504hr,在ASTM#3油中 | ISO 175 | -2.0 | - | |
| 体积变化 | 23°C,70hr,A级标准燃料 | ASTM D471 | 0.0 | % |
| 空气中拉伸强度的变化率 | 300%应变,100°C,168hr,在ASTM#3油中 | ISO 175 | -11 | % |
| 100°C,336hr,在ASTM#3油中 | ISO 175 | -3.0 | % | |
| 100%应变,100°C,336hr,在ASTM#3油中 | ISO 175 | -2.0 | % | |
| 300%应变,100°C,336hr,在ASTM#3油中 | ISO 175 | -9.0 | % | |
| 100°C,504hr,在ASTM#3油中 | ISO 175 | 1.0 | % | |
| 300%应变,23°C,504hr,在参考燃料A中（异辛烷） | ISO 175 | -4.0 | % | |
| 100°C,70hr,在ASTM#3油中 | ISO 175 | 10 | % | |
| 100°C,70hr | ASTMD573 | 2.0 | % | |
| 100%应变,100°C,70hr | ASTM D573 | 4.0 | % | |
| 300%应变,100°C,70hr | ASTM D573 | 2.0 | % | |
| 300%应变,100°C,70hr,在ASTM#3油中 | ASTM D471 | 3.0 | % | |
| 100°C,168hr,在ASTM#1油中 | ASTMD471 | 0.0 | % | |
| 23°C,504hr,inReferenceFuelC | ISO 175 | -15 | % | |
| 100%应变,23°C,504hr,inReferenceFuelC | ISO 175 | -36 | % | |
| 300%应变,23°C,504hr,inReferenceFuelC | ISO 175 | -51 | % | |
| 23°C,504hr,在参考燃料A中（异辛烷） | ISO 175 | 13 | % | |
| 100%应变,23°C,504hr,在参考燃料A中（异辛烷） | ISO 175 | -4.0 | % | |
| 23°C,70hr,在参考燃料A中（异辛烷） | ISO 175 | 16 | % | |
| 300%应变,23°C,336hr,C级标准燃料 | ASTM D471 | -33 | % | |
| 23°C,336hr,在基准燃料A中 | ASTM D471 | 7.0 | % | |
| 100%应变,23°C,336hr,在基准燃料A中 | ASTM D471 | 1.0 | % | |
| 300%应变,23°C,336hr,在基准燃料A中 | ASTM D471 | 3.0 | % | |
| 23°C,504hr,C级标准燃料 | ASTM D471 | -15 | % | |
| 300%应变,125°C,168hr | ASTM D573 | -18 | % | |
| 125°C,336hr | ASTMD573 | -40 | % | |
| 300%应变125°C,336hr | ISO 216 | -22 | % | |
| 100%应变125°C,504hr | ISO 216 | -5.0 | % | |
| 300%应变125°C,504hr | ISO 216 | -25 | % | |
| 100%应变,100°C,168hr,在ASTM#1油中 | ASTMD471 | 4.0 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,23°C,336hr,在基准燃料A中 | ASTM D471 | 0.0 | - |
| 支撐D,23°C,504hr,inReferenceFuelC | ASTMD471 | -13 | - | |
| 支撐D,23°C,504hr,在基准燃料A中 | ASTM D471 | 2.0 | - | |
| 支撐D,100°C,70hr,在ASTM#1油中 | ASTMD471 | 0.0 | - | |
| 支撐D,100°C,70hr,在ASTM#3油中 | ASTM D471 | 5.0 | - | |
| 支撐D,100°C,168hr,在ASTM#1油中 | ASTMD471 | 2.0 | - | |
| 支撐D,100°C,168hr,在ASTM#3油中 | ASTM D471 | 5.0 | - | |
| 支撐D,100°C,336hr,在ASTM#1油中 | ASTMD471 | 0.0 | - | |
| 支撐D,100°C,336hr,在ASTM#3油中 | ASTM D471 | -4.0 | - | |
| 体积变化 | 23°C,336hr,在基准燃料A中 | ISO 175 | 1.0 | % |
| 23°C,336hr,C级标准燃料 | ASTM D471 | 26 | % | |
| 23°C,504hr,A级标准燃料 | ASTM D471 | 1.0 | % | |
| 23°C,504hr,C级标准燃料 | ASTM D471 | 26 | % | |
| 100°C,70hr,ASTM标准油（1号） | ASTM D471 | 0.0 | % | |
| 100°C,70hr,ASTM标准油（3号） | ASTM D471 | 9.0 | % | |
| 100°C,168hr,ASTM标准油（1号） | ASTM D471 | 0.0 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,23°C,70hr,在基准燃料A中（异辛烷） | ISO 175 | 1.0 | - |
| 支撐D,23°C,168hr,在基准燃料A中（异辛烷） | ISO 175 | 1.0 | - | |
| 支撐D,23°C,336hr,在基准燃料A中（异辛烷） | ISO 175 | 0.0 | - | |
| 支撐D,23°C,504hr,在基准燃料A中（异辛烷） | ISO 175 | 2.0 | - | |
| 空气中拉伸强度的变化率 | 300%应变125°C,70hr | ISO 216 | -7.0 | % |
| 100%应变125°C,168hr | ISO 216 | 4.0 | % | |
| 300%应变125°C,168hr | ISO 216 | -18 | % | |
| 100%应变125°C,336hr | ISO 216 | 0.0 | % | |
| 100%应变,100°C,336hr | ASTM D573 | 4.0 | % | |
| 300%应变,100°C,336hr | ASTM D573 | -2.0 | % | |
| 100°C,504hr | ASTMD573 | 3.0 | % | |
| 100%应变,100°C,504hr | ASTM D573 | 5.0 | % | |
| 300%应变,100°C,504hr | ASTM D573 | -3.0 | % | |
| 125°C,70hr | ASTMD573 | -11 | % | |
| 100%应变,125°C,70hr | ASTM D573 | 1.0 | % | |
| 300%应变,125°C,70hr | ASTM D573 | -7.0 | % | |
| 125°C,168hr | ASTMD573 | -27 | % | |
| 100%应变,125°C,168hr | ASTM D573 | 4.0 | % | |
| 300%应变,23°C,70hr,在基准燃料A中 | ASTM D471 | 0.0 | % | |
| 23°C,168hr,C级标准燃料 | ASTM D471 | -17 | % | |
| 100%应变,23°C,168hr,C级标准燃料 | ASTM D471 | -36 | % | |
| 300%应变,23°C,168hr,C级标准燃料 | ASTM D471 | -30 | % | |
| 23°C,168hr,在基准燃料A中 | ASTM D471 | 16 | % | |
| 100%应变,23°C,168hr,在基准燃料A中 | ASTM D471 | 6.0 | % | |
| 100%应变,23°C,336hr,inReferenceFuelC | ISO 175 | -36 | % | |
| 300%应变,23°C,336hr,inReferenceFuelC | ISO 175 | -33 | % | |
| 23°C,336hr,在参考燃料A中（异辛烷） | ISO 175 | 7.0 | % | |
| 100%应变,23°C,336hr,在参考燃料A中（异辛烷） | ISO 175 | 1.0 | % | |
| 300%应变,23°C,336hr,在参考燃料A中（异辛烷） | ISO 175 | 3.0 | % | |
| 300%应变,100°C,168hr,在ASTM#1油中 | ASTMD471 | 0.0 | % | |
| 100°C,168hr,在ASTM#3油中 | ASTM D471 | 12 | % | |
| 100%应变,100°C,168hr,在ASTM#3油中 | ASTM D471 | -7.0 | % | |
| 空气中硬度(Shore)的变化率 | 支撐D,125°C,168hr | ASTMD573 | -1.0 | - |
| 支撐D,125°C,336hr | ASTMD573 | -1.0 | - | |
| 支撐D,125°C,504hr | ASTMD573 | 1.0 | - | |
| 空气中拉伸强度的变化率 | 23°C,70hr,C级标准燃料 | ASTM D471 | -17 | % |
| 空气中极限伸长率的变化率 | 23°C,336hr,inReferenceFuelC | ISO 175 | -5.0 | % |
| 23°C,336hr,在参考燃料A中（异辛烷） | ISO 175 | 3.0 | % | |
| 23°C,504hr,inReferenceFuelC | ISO 175 | -2.0 | % | |
| 23°C,504hr,C级标准燃料 | ASTM D471 | -2.0 | % | |
| 23°C,504hr,在基准燃料A中 | ASTM D471 | 8.0 | % | |
| 100°C,70hr,在ASTM#1油中 | ASTMD471 | 18 | % | |
| 100°C,70hr,在ASTM#3油中 | ASTM D471 | 17 | % | |
| 100°C,168hr,在ASTM#1油中 | ASTMD471 | 19 | % | |
| 100°C,168hr,在ASTM#3油中 | ASTM D471 | 25 | % | |
| 100°C,336hr,在ASTM#1油中 | ASTMD471 | 23 | % | |
| 23°C,504hr,在参考燃料A中（异辛烷） | ISO 175 | 8.0 | % | |
| 100°C,70hr,在ASTM#3油中 | ISO 175 | 17 | % | |
| 100°C,168hr,在ASTM#3油中 | ISO 175 | 25 | % | |
| 100°C,336hr,在ASTM#3油中 | ISO 175 | 27 | % | |
| 100°C,504hr,在ASTM#3油中 | ISO 175 | 38 | % | |
| 体积变化 | 100°C,168hr,ASTM标准油（3号） | ASTM D471 | 10 | % |
| 100°C,336hr,ASTM标准油（1号） | ASTM D471 | 0.0 | % | |
| 100°C,336hr,ASTM标准油（3号） | ASTM D471 | 12 | % | |
| 100°C,504hr,ASTM标准油（1号） | ASTM D471 | 0.0 | % | |
| 100°C,504hr,ASTM标准油（3号） | ASTM D471 | 13 | % | |
| 23°C,70hr,在基准燃料A中 | ISO 175 | 0.0 | % | |
| 23°C,70hr,在基准燃料C中 | ISO 175 | 22 | % | |
| 23°C,168hr,在基准燃料A中 | ISO 175 | 1.0 | % | |
| 23°C,168hr,在基准燃料C中 | ISO 175 | 26 | % | |
| 空气中拉伸强度的变化率 | 100%应变,100°C,504hr,在ASTM#3油中 | ISO 175 | -9.0 | % |
| 300%应变,100°C,504hr,在ASTM#3油中 | ISO 175 | -18 | % | |
| 空气中极限伸长率的变化率 | 23°C,70hr,C级标准燃料 | ASTM D471 | 0.0 | % |
| 23°C,70hr,在基准燃料A中 | ASTM D471 | 5.0 | % | |
| 23°C,168hr,C级标准燃料 | ASTM D471 | -6.0 | % |
【免责声明】
普拉司网尽最大努力确保此数据的准确性，但是普拉司网对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。