完善物性
EHMWPE Generic UHMWPE Generic
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
特性：
机械性能
物性表
| 测试条件 | 测试方法 | 测试结果 | 测试单位 | |
|---|---|---|---|---|
| 拉伸应变 | 屈服,23°C | ISO 527-2 | 15to20 | % |
| 断裂,23°C | ASTM D638 | 59to470 | % | |
| 耗散因数 | 23°C | ASTM D150 | -2.0E-3到3.9E-3 | - |
| 23°C | IEC 60250 | 3.7E-4到1.0E-3 | - | |
| 拉伸应变 | 断裂,23°C | ISO 527-2 | 350to400 | % |
| 标称拉伸断裂应变 | 23°C | ISO 527-2 | 50to56 | % |
| 弯曲模量 | 23°C | ASTM D790 | 441to915 | MPa |
| 弯曲强度 | 屈服,23°C | ASTM D790 | 20.6to26.3 | MPa |
| 压缩模量 | - | ASTM D695 | 551to689 | MPa |
| 压缩强度 | 23°C | ASTM D695 | 20.0to22.9 | MPa |
| 23°C | ISO 604 | 4.00to32.0 | MPa | |
| 摩擦系数 | - | ASTM D1894 | 0.060to0.16 | - |
| 硬度 | 23°C | ASTM D2240 | 59to66 | - |
| 23°C | ISO 868 | 57to64 | - | |
| 球压硬度 | - | ISO 2039-1 | 35.0to38.3 | MPa |
| 拉伸模量 | 23°C | ASTM D638 | 669to803 | MPa |
| 23°C | ISO 527-2 | 676to795 | MPa | |
| 拉伸强度 | 屈服,23°C | ASTM D638 | 16.7to23.5 | MPa |
| 屈服,23°C | ISO 527-2 | 17.0to17.6 | MPa | |
| 断裂,23°C | ASTM D638 | 29.6to53.5 | MPa | |
| 断裂,23°C | ISO 527-2 | 30.0to30.2 | MPa | |
| 表面电阻率 | -- | IEC 60093 | 1.0E+6到2.5E+12 | ohms |
| 体积电阻率 | 23°C | ASTM D257 | 1.0E+6到1.0E+15 | ohms·cm |
| 23°C | IEC 60093 | 9.8E+13到1.0E+14 | ohms·cm | |
| 介电强度 | 23°C | ASTM D149 | 14to91 | kV/mm |
| 23°C | IEC 60243-1 | 45to46 | kV/mm | |
| 介电常数 | 23°C | ASTM D150 | 2.28to3.00 | - |
| 23°C | IEC 60250 | 2.55 | - | |
| 简支梁缺口冲击强度 | 23°C | ISO 179 | 78to180 | kJ/m² |
| 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 78.9to93.5 | °C |
| 1.8MPa,未退火 | ASTM D648 | 45.9to79.0 | °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 42.0to42.1 | °C | |
| 连续使用温度 | - | ASTM D794 | 80.0to120 | °C |
| 维卡软化温度 | - | ASTMD1525 | 80.0to128 | °C |
| 熔融温度 | - | ASTM D3418 | 133to136 | °C |
| 结晶峰温度 | DSC | ASTM D3418 | 127to135 | °C |
| 线性热膨胀系数 | MD：-- | ASTM D696 | 9.0E-5到9.2E-4 | cm/cm/°C |
| MD：-- | ISO 11359-2 | 2E-04 | cm/cm/°C | |
| 拉伸强度 | 极限,23°C | ASTM D638 | 32.8to40.0 | MPa |
| 密度 | -- | ASTM D792 | 0.922to0.949 | g/cm³ |
| 23°C | ISO 1183 | 0.930to0.950 | g/cm³ | |
| -- | ASTM D1505 | 0.924to0.954 | g/cm³ | |
| 表观密度 | - | ASTM D1895 | 0.45 | g/cm³ |
| 熔体质量流动速率 | 190°C/21.6kg | ASTM D1238 | 0.0to0.25 | g/10min |
| 收缩率 | MD：23°C | ASTM D955 | 2.2to8.1 | % |
| 吸水率 | 23°C,24hr | ASTM D570 | 0.010to0.070 | % |
| 饱和,23°C | ISO 62 | 0.010to0.020 | % | |
| 比热 | 23°C | ASTMC351 | 1840to2010 | J/kg/°C |
| 导热系数 | 23°C | ASTMC177 | 0.39to0.41 | W/m/K |
| 表面电阻率 | -- | ASTM D257 | 1.0E+3到2.5E+13 | ohms |