完善物性
LLDPE ∞ 美国杜邦
0
参考价： 0 元/吨
产品描述物性表认证信息替代型号(0)
产品描述
特性：
良好粘结性
物性表
| 物理性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
|---|---|---|---|---|
| 密度 | - | ASTM D792 | 0.930 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 4.2 | g/10 min |
| 密度 | - | ASTM D792 | 0.940 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 4.7 | g/10 min |
| 密度 | - | ASTM D792 | 0.920 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 2.5 | g/10 min |
| 密度 | - | ASTM D792 | 0.910 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 1.7 | g/10 min |
| 密度 | - | ASTM D792 | 0.920 | g/cm³ |
| - | ASTM D792 | 0.910 | g/cm³ | |
| - | ASTM D792 | 0.930 | g/cm³ | |
| 熔体质量流动速率 | - | ASTM D1238 | 3.0 | g/10 min |
| 密度 | - | ASTM D792 | 0.900 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 1.7 | g/10 min |
| 密度 | - | ASTM D792 | 0.920 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 1.8 | g/10 min |
| 密度 | - | ASTM D792 | 0.920 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 7.0 | g/10 min |
| 密度 | - | ASTM D792 | 0.910 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 1.7 | g/10 min |
| - | ASTM D1238 | 2.5 | g/10 min | |
| 密度 | - | ASTM D792 | 0.910 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 2.2 | g/10 min |
| 密度 | - | ASTM D792 | 0.919 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 5.8 | g/10 min |
| 密度 | - | ASTM D792 | 0.920 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 1.5 | g/10 min |
| 密度 | - | ASTM D792 | 0.910 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 2.7 | g/10 min |
| 密度 | - | ASTM D792 | 0.940 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 3.3 | g/10 min |
| - | ASTM D1238 | 1.1 | g/10 min | |
| 密度 | - | ASTM D792 | 0.920 | g/cm³ |
| 熔体质量流动速率 | - | ASTM D1238 | 3.4 | g/10 min |
| 热性能 | 测试条件 | 测试方法 | 测试结果 | 测试单位 |
| 维卡软化温度 | - | ASTM D1525 | 91.0 | °C |
| 熔融温度 | - | ASTM D1525 | 121 | °C |
| Freezing Point | - | ASTM D3418 | 196 | °C |
| 维卡软化温度 | - | ASTM D1525 | 82.0 | °C |
| 熔融温度 | - | ASTM D1525 | 109 | °C |
| 凝固点 | - | Freezing Point | 103 | °C |
| 维卡软化温度 | - | ASTM D1525 | 108 | °C |
| 熔融温度 | - | ASTM D1525 | 126 | °C |
| 维卡软化温度 | - | ASTM D1525 | 100 | °C |
| 熔融温度 | - | ASTM D1525 | 125 | °C |
| Freezing Point | - | ASTM D3418 | 109 | °C |
| 维卡软化温度 | - | ASTM D1525 | 78.0 | °C |
| 熔融温度 | - | ASTM D1525 | 122 | °C |
| 维卡软化温度 | - | ASTM D1525 | 92.8 | °C |
| 熔融温度 | - | ASTM D1525 | 127 | °C |
| 维卡软化温度 | - | ASTM D1525 | 71.0 | °C |
| 熔融温度 | - | ASTM D1525 | 119 | °C |
| 维卡软化温度 | - | ASTM D1525 | 100 | °C |
| 熔融温度 | - | ASTM D1525 | 212 | °C |
| 凝固点 | - | ASTM D3418 | 106 | °C |
| 熔融温度 | - | ASTM D1525 | 120 | °C |
| 维卡软化温度 | - | ASTM D1525 | 101 | °C |
| 熔融温度 | - | ASTM D1525 | 111 | °C |
| 凝固点 | - | ASTM D3418 | 106 | °C |
| 维卡软化温度 | - | ASTM D1525 | 84.0 | °C |
| 熔融温度 | - | ASTM D1525 | 119 | °C |
| 维卡软化温度 | - | ASTM D1525 | 87.2 | °C |
| 熔融温度 | - | ASTM D1525 | 121 | °C |
| 维卡软化温度 | - | ASTM D1525 | 100 | °C |
| 熔融温度 | - | ASTM D1525 | 127 | °C |
| 凝固点 | - | ASTM D3418 | 114 | °C |
| 维卡软化温度 | - | ASTM D1525 | 91.0 | °C |
| - | ASTM D1525 | 102 | °C | |
| 熔融温度 | - | ASTM D1525 | 125 | °C |
| 维卡软化温度 | - | ASTM D1525 | 103 | °C |
| 熔融温度 | - | ASTM D1525 | 115 | °C |
| 凝固点 | - | ASTM D3418 | 98 | °C |
| 维卡软化温度 | - | ASTM D1525 | 77.0 | °C |
| 熔融温度 | - | ASTM D1525 | 120 | °C |
| 维卡软化温度 | - | ASTM D1525 | 105 | °C |
| 熔融温度 | - | ASTM D1525 | 126 | °C |